Recent experimentally validated alloy design theories have demonstrated nanocrystalline binary alloys that are stable against thermally induced grain growth. An open question is whether such thermal stability also translates to stability under irradiation. In this study, we investigate the response to heavy ion irradiation of a nanocrystalline platinum gold alloy that is known to be thermally stable from previous studies. Heavy ion irradiation was conducted at both room temperature and elevated temperatures on films of nanocrystalline platinum and platinum gold. Using scanning/transmission electron microscopy equipped with energy-dispersive spectroscopy and automated crystallographic orientation mapping, we observe substantial grain growth in the irradiated area compared to the controlled area beyond the range of heavy ions, as well as compositional redistribution under these conditions, and discuss mechanisms underpinning this instability. These findings highlight that grain boundary stability against one external stimulus, such as heat, does not always translate into grain boundary stability under other stimuli, such as displacement damage.
High-throughput image segmentation of atomic resolution electron microscopy data poses an ongoing challenge for materials characterization. In this paper, we investigate the application of the polyhedral template matching (PTM) method, a technique widely employed for visualizing three-dimensional (3D) atomistic simulations, to the analysis of two-dimensional (2D) atomic resolution electron microscopy images. This technique is complementary with other atomic resolution data reduction techniques, such as the centrosymmetry parameter, that use the measured atomic peak positions as the starting input. Furthermore, since the template matching process also gives a measure of the local rotation, the method can be used to segment images based on local orientation. We begin by presenting a 2D implementation of the PTM method, suitable for atomic resolution images. We then demonstrate the technique's application to atomic resolution scanning transmission electron microscopy images from close-packed metals, providing examples of the analysis of twins and other grain boundaries in FCC gold and martensite phases in 304 L austenitic stainless steel. Finally, we discuss factors, such as positional errors in the image peak locations, that can affect the accuracy and sensitivity of the structural determinations.
A thermally driven, micrometer-scale switch technology has been created that utilizes the ErH3/Er2O3 materials system. The technology is comprised of novel thin film switches, interconnects, on-board micro-scale heaters for passive thermal environment sensing, and on-board micro-scale heaters for individualized switch actuation. Switches undergo a thermodynamically stable reduction/oxidation reaction leading to a multi-decade (>11 orders) change in resistance. The resistance contrast remains after cooling to room temperature, making them suitable as thermal fuses. An activation energy of 290 kJ/mol was calculated for the switch reaction, and a thermos-kinetic model was employed to determine switch times of 120 ms at 560 °C with the potential to scale to 1 ms at 680 °C.
Adams, David P.; Mcclure, Zachary D.; Appleton, Robert J.; Strachan, Alejandro
Ge-Sb-Te (GST) alloys are leading phase-change materials for data storage due to the fast phase transition between amorphous and crystalline states. Ongoing research aims at improving the stability of the amorphous phase to improve retention. This can be accomplished by the introduction of carbon as a dopant to Ge2Sb2Te5, which is known to alter the short- and mid-range structure of the amorphous phase and form covalently bonded C clusters, both of which hinder crystallization. The relative importance of these processes as a function of C concentration is not known. We used molecular dynamics simulation based on density functional theory to study how carbon doping affects the atomic structure of GST-C. Carbon doping results in an increase in tetrahedral coordination, especially of Ge atoms, and this is known to stabilize the amorphous phase. We observe an unexpected, non-monotonous trend in the number of tetrahedral bonded Ge with the amount of carbon doping. Our simulations show an increase in the number of tetrahedral bonded Ge up to 5 at.% C, after which the number saturates and begins to decrease above 14 at.% C. The carbon atoms aggregate into clusters, mostly in the form of chains and graphene flakes, leaving less carbon to disrupt the GST matrix at higher carbon concentrations. Different degrees of carbon clustering can explain divergent experimental results for recrystallization temperature for carbon doped GST.
Bimetallic, reactive multilayers are uniformly structured materials composed of alternating sputter-deposited layers that may be ignited to produce self-propagating mixing and formation reactions. These nanolaminates are most commonly used as rapid-release heat sources. The specific chemical composition at each metal/metal interface determines the rate of mass transport in a mixing and formation reaction. The inclusion of engineered diffusion barriers at each interface will not only inhibit solid-state mixing but also may impede the self-propagating reactions by introducing instabilities to wavefront morphology. This work examines the effect of adding diffusion barriers on the propagation of reaction waves in Co/Al multilayers. The Co/Al system has been shown to exhibit a reaction propagation instability that is dependent on the bilayer thickness, which allows for the occurrence of unstable modes in otherwise stable designs from the inclusion of diffusion barriers. Based on the known stability criteria in the Co/Al multilayer system, the way in which the inclusion of diffusion barriers changes a multilayer's heat of reaction, thermal conductivity, and material mixing mechanisms can be determined. These factors, in aggregate, lead to changes in the wavefront velocity and stability.
The propagation of self-sustained formation reactions in sputter-deposited Co/Al multilayers is known to exhibit a design-dependent instability. Multilayers having thin bilayers (<55 nm period) exhibit stable propagating waves, whereas those with a larger period react unstably. The specific two-dimensional (2D) instability observed involves the transverse propagation of a band in front of a stalled front commonly referred to as a “spin band.” Previous finite-element studies have shown that these instabilities are thermodynamically driven by the forward conduction of heat away from the flame front. However, the magnitude of that loss is inherently tied to the bilayer design in traditional bimetallic multilayers, which couples any proposed stability criteria to a varying critical diffusion distance. This work utilizes a recently developed class of materials known as “inert-mediated reactive multilayers” to decouple the thermodynamic and kinetic contributions to propagating wave stability by reducing the stored chemical energy density in normally stable bilayer designs. By depositing an inert product phase (B2-CoAl) within the mid-plane of Co and Al reactant layers, spin instabilities arise as a function of both diluted volume and critical diffusion distance. From there, a stability criterion is determined for Co/Al multilayers based on enthalpy loss from the reaction zone, and its physical significance is explored.
Multimodal datasets of materials are rich sources of information which can be leveraged for expedited discovery of process–structure–property relationships and for designing materials with targeted structures and/or properties. For this data descriptor article, we provide a multimodal dataset of magnetron sputter-deposited molybdenum (Mo) thin films, which are used in a variety of industries including high temperature coatings, photovoltaics, and microelectronics. In this dataset we explored a process space consisting of 27 unique combinations of sputter power and Ar deposition pressure. Here, the phase, structure, surface morphology, and composition of the Mo thin films were characterized by x-ray diffraction, scanning electron microscopy, atomic force microscopy, and Rutherford backscattering spectrometry. Physical properties—namely, thickness, film stress and sheet resistance—were also measured to provide additional film characteristics and behaviors. Additionally, nanoindentation was utilized to obtain mechanical load-displacement data. The entire dataset consists of 2072 measurements including scalar values (e.g., film stress values), 2D linescans (e.g., x-ray diffractograms), and 3D imagery (e.g., atomic force microscopy images). An additional 1889 quantities, including film hardness, modulus, electrical resistivity, density, and surface roughness, were derived from the experimental datasets using traditional methods. Minimal analysis and discussion of the results are provided in this data descriptor article to limit the authors’ preconceived interpretations of the data. Overall, the data modalities are consistent with previous reports of refractory metal thin films, ensuring that a high-quality dataset was generated. The entirety of this data is committed to a public repository in the Materials Data Facility.
Chalcogenide thin films that undergo reversible phase changes show promise for use in next-generation nanophotonics, microelectronics, and other emerging technologies. One of the many studied compounds, Ge 2 Sb 2 Te 5 , has demonstrated several useful properties and performance characteristics. However, the efficacy of benchmark Ge 2 Sb 2 Te 5 is restricted by amorphous phase thermal stability below ∼150 °C, limiting its potential use in high-temperature applications. In response, previous studies have added a fourth species (e.g., C) to sputter-deposited Ge 2 Sb 2 Te 5 , demonstrating improved thermal stability. Our current research confirms reported thermal stability enhancements and assesses the effects of carbon on crystalline phase radiation response. Through in situ transmission electron microscope irradiation studies, we examine the effect of C addition on the amorphization behavior of initially cubic and trigonal polycrystalline films irradiated using 2.8 MeV Au to various doses up to 1 × 10 15 cm −2 . It was found that increased C content reduces radiation tolerance of both cubic and trigonal phases.
Nanocrystalline metals are inherently unstable against thermal and mechanical stimuli, commonly resulting in significant grain growth. Also, while these metals exhibit substantial Hall-Petch strengthening, they tend to suffer from low ductility and fracture toughness. With regard to the grain growth problem, alloying elements have been employed to stabilize the microstructure through kinetic and/or thermodynamic mechanisms. And to address the ductility challenge, spatially-graded grain size distributions have been developed to facilitate heterogeneous deformation modes: high-strength at the surface and plastic deformation in the bulk. In the present work, we combine these two strategies and present a new methodology for the fabrication of gradient nanostructured metals via compositional means. We have demonstrated that annealing a compositionally stepwise Pt-Au film with a homogenous microstructure results in a film with a spatial microstructural gradient, exhibiting grains which can be twice as wide in the bulk compared to the outer surfaces. Additionally, phase-field modeling was employed for the comparison with experimental results and for further investigation of the competing mechanisms of Au diffusion and thermally induced grain growth. This fabrication method offers an alternative approach for developing the next generation of microstructurally stable gradient nanostructured films.
Nanothermite NiO-Al is a promising material system for low gas emission heat sources; yet, its reactive properties are highly dependent on material processing conditions. In the current study, sputter deposition is used to fabricate highly controlled nanolaminates comprised of alternating NiO and Al layers. Films having an overall stoichiometry of 2Al to 3NiO were produced with different bilayer thicknesses to investigate how ignition and self-sustained, high temperature reactions vary with changes to nanometer-scale periodicity and preheat conditions. Ignition studies were carried out with both hot plate and laser irradiation and compared to slow heating studies in hot-stage x-ray diffraction. Ignition behavior has bilayer thickness and heating rate dependencies. The 2Al/3NiO with λ ≤ 300 nm ignited via solid/solid diffusion mixing (activation energy, Ea = 49 ± 3 kJ/mole). Multilayers having λ≥ 500 nm required a more favorable mixing kinetics of solid/liquid dissolution into molten Al (Ea = 30 ± 4 kJ/mole). This solid/liquid dissolution Ea is a factor of 5 lower than that of the previously reported powder compacts due to the elimination of a passivating Al oxide layer present on the powder. The reactant mixing mechanism between 300 and 500 nm bilayer thicknesses was dependent on the ignition source's heating rate. The self-propagating reaction velocities of 2Al/3NiO multilayers varied from 0.4 to 2.5 m/s. Pre-heating nanolaminates to temperatures below the onset reaction temperatures associated with forming intermediate nickel aluminides at multilayer interfaces led to increased propagation velocities, whereas pre-heating samples above the onset temperatures inhibited subsequent attempts at laser ignition.
Metals subjected to irradiation environments undergo microstructural evolution and concomitant degradation, yet the nanoscale mechanisms for such evolution remain elusive. Here, we combine in situ heavy ion irradiation, atomic resolution microscopy, and atomistic simulation to elucidate how radiation damage and interfacial defects interplay to control grain boundary (GB) motion. While classical notions of boundary evolution under irradiation rest on simple ideas of curvature-driven motion, the reality is far more complex. Focusing on an ion-irradiated Pt Σ3 GB, we show how this boundary evolves by the motion of 120° facet junctions separating nanoscale {112} facets. Our analysis considers the short- and mid-range ion interactions, which roughen the facets and induce local motion, and longer-range interactions associated with interfacial disconnections, which accommodate the intergranular misorientation. We suggest how climb of these disconnections could drive coordinated facet junction motion. These findings emphasize that both local and longer-range, collective interactions are important to understanding irradiation-induced interfacial evolution.
Reactive Co/Al multilayers are uniformly structured materials that may be ignited to produce rapid and localized heating. Prior studies varying the bilayer thickness (i.e., sum of two individual layers of Co and Al) have revealed different types of flame morphologies, including: (a) steady/planar, (b) wavy/periodic, and (c) transverse bands, originating in the flame front. These instabilities resemble the “spin waves” first observed in the early studies of solid combustion (i.e., Ti cylinder in a N2 atmosphere), and are likewise thought to be due to the balance of heat released by reaction and heat conduction forward into the unreacted multilayer. However, the multilayer geometry and three-dimensional (3D) edge effects are relatively unexplored. In this work, a new diffusion-limited reaction model for Co/Al multilayers was implemented in large, novel 3D finite element analysis (FEA) simulations, in order to study the origins of these spinlike flames. This reaction model builds upon previous work by introducing three new phase-dependent property models for: (1) the diffusion coefficient, (2) anisotropic thermal conductivity tensor, and (3) bulk heat capacity, as well as one additional model for the bilayer-dependent heat of reaction. These novel 3D simulations are the first to predict both steady and unsteady flames in Co/Al multilayers. Moreover, two unsteady modes of flame propagation are identified, which depend on the enhanced conduction losses with slower flames, as well as flame propagation around notched edges. Future work will consider the generality of the current modeling approach and also seek to define a more generalized set of stability criteria for additional multilayer systems.