Two novel LiCl·DMSO polymer structures were created by combining dry LiCl salt with dimethyl sulfoxide (DMSO), namely, catena-poly[[chloridolithium(I)]-μ-(dimethyl sulfoxide)-κ2O:O-[chloridolithium(I)]-di-μ-(dimethyl sulfoxide)-κ4O:O], [Li2Cl2(C2H6OS)3]n, and catena-poly[lithium(I)-μ-chlorido-μ-(dimethyl sulfoxide)-κ2O:O], [LiCl(C2H6OS)]n. The initial synthesized phase had very small block-shaped crystals (<0.08 mm) with monoclinic symmetry and a 2 LiCl: 3 DMSO ratio. As the solution evaporated, a second phase formed with a plate-shaped crystal morphology. After about 20 minutes, large (>0.20 mm) octahedron-shaped crystals formed. The plate crystals and the octahedron crystals are the same tetragonal structure with a 1 LiCl: 1 DMSO ratio. These structures are reported and compared to other known LiCl·solvent compounds.
Neural ordinary differential equations (NODEs) have recently regained popularity as large-depth limits of a large class of neural networks. In particular, residual neural networks (ResNets) are equivalent to an explicit Euler discretization of an underlying NODE, where the transition from one layer to the next is one time step of the discretization. The relationship between continuous and discrete neural networks has been of particular interest. Notably, analysis from the ordinary differential equation viewpoint can potentially lead to new insights for understanding the behavior of neural networks in general. In this work, we take inspiration from differential equations to define the concept of stiffness for a ResNet via the interpretation of a ResNet as the discretization of a NODE. Here, we then examine the effects of stiffness on the ability of a ResNet to generalize, via computational studies on example problems coming from climate and chemistry models. We find that penalizing stiffness does have a unique regularizing effect, but we see no benefit to penalizing stiffness over L2 regularization (penalization of network parameter norms) in terms of predictive performance.
Earth’s environment can be considered especially harsh due to the cyclic exposure of heat, moisture, oxygen, and ultraviolet (UV) and visible light. Polymer-derived materials subjected to these conditions over time often exhibit symptoms of degradation and deterioration, ultimately leading to accelerated material failure. To combat this, chemical additives known as antioxidants are often used to delay the onset of weathering and oxidative degradation. Phenol-derived antioxidants have been used for decades due to their excellent performance and stability; unfortunately, concerns regarding their toxicity and leaching susceptibility have driven researchers to identify novel solutions to replace phenolic antioxidants. Herein, we report on the antioxidant efficacy of organoborons, which have been known to exhibit antioxidant activity in plants and animals. Four different organoboron molecules were formulated into epoxy materials at various concentrations and subsequently cured into thermoset composites. Their antioxidant performance was subsequently analyzed via thermal, colorimetric, and spectroscopic techniques. Generally, thermal degradation and oxidation studies proved inconclusive and ambiguous. However, aging studies performed under thermal and UV-intensive conditions showed moderate to extreme color changes, suggesting poor antioxidant performance of all organoboron additives. Infrared spectroscopic analysis of the UV aged samples showed evidence of severe material oxidation, while the thermally aged samples showed only slight material oxidation. Solvent extraction experiments showed that even moderately high organoboron concentrations show negligible leaching susceptibility, confirming previously reported results. This finding may have benefits in applications where additive leaching may cause degradation to sensitive materials, such as microelectronics and other materials science related areas.
A natural clinoptilolite sample near the Nevada National Security Site was obtained to study adsorption and retardation on gas transport. Of interest is understanding the competition for adsorption sites that may reduce tracer gas adsorption relative to single-component measurements, which may be affected by the multi-scale pore structure of clinoptilolite. Clinoptilolite has three distinct domains of pore size distributions ranging from nanometers to micrometers: micropores with 0.4–0.7 nm diameters, measured on powders by CO2 adsorption at 273 K, representing the zeolite cages; mesopores with 4–200 nm diameters, observed using liquid nitrogen adsorption at 77 K; and macropores with 300–1000 nm diameters, measured by mercury injection on rock chips (~ 100 mesh), likely representing the microfractures. These pore size distributions are consistent with X-ray computed tomography (CT) and focused ion beam scanning electron microscope (FIB-SEM) images, which are used to construct the three-dimensional (3D) pore network to be used in future gas transport modeling. To quantify tracer gas adsorption in this multi-scale pore structure and multicomponent gas species environment, natural zeolite samples initially in equilibrium in air were exposed to a mixture of tracer gases. As the tracer gases diffuse and adsorb in the sample, the remaining tracer gases outside the sample fractionate. Using a quadrupole mass spectrometer to quantify this fractionation, the degree of adsorption of tracer gases in the multicomponent gas environment and multi-scale pore structure is assessed. The major finding is that Kr reaches equilibrium much faster than Xe in the presence of ambient air, which leads to more Kr uptake than Xe over limited exposure periods. When the clinoptilolite chips were exposed to humid air, the adsorption capability decreases significantly for both Xe and Kr with relative humidity (RH) as low as 3%. Both Xe and Kr reaches equilibrium faster at higher RH. The different, unexpected, adsorption behavior for Xe and Kr is due to their kinetic diameters similar to the micropores in clinoptilolite which makes it harder for Xe to access compared to Kr.
We evaluate neural radiance fields (NeRFs) as a method for reconstructing 3D volumetric scenes from low Earth orbit satellite imagery. We leverage commercial satellite data to reconstruct a scene using existing software tools. In doing so, we identify difficulties in these mapping datasets for NeRF generation. We propose potential applications in geospatial intelligence for context and improved image interpretation.