The need for clean, renewable energy has driven the expansion of renewable energy generators, such as wind and solar. However, to achieve a robust and responsive electrical grid based on such inherently intermittent renewable energy sources, grid-scale energy storage is essential. The unmet need for this critical component has motivated extensive grid-scale battery research, especially exploring chemistries “beyond Li-ion”. Among others, molten sodium (Na) batteries, which date back to the 1960s with Na-S, have seen a strong revival, owing mostly to raw material abundance and the excellent electrochemical properties of Na metal. Recently, many groups have demonstrated important advances in battery chemistries, electrolytes, and interfaces to lower material and operating costs, enhance cyclability, and understand key mechanisms that drive failure in molten Na batteries. For widespread implementation of molten Na batteries, though, further optimization, cost reduction, and mechanistic insight is necessary. In this light, this work provides a brief history of mature molten Na technologies, a comprehensive review of recent progress, and explores possibilities for future advancements.
The DOE Office of Electricity views sodium batteries as a priority in pursuing a safe, resilient, and reliable grid. Improvements in solid-state electrolytes are key to realizing the potential of these large-scale batteries. NaSICON structure consists of SiO4 or PO4 tetrahedra sharing common corners with ZrO6 octahedra. Structure forms “tunnels” in three dimensions that can transport interstitial sodium ion. 3D structure provides higher ionic conductivity than other conductors (β’’-alumina), particularly at low temperature. Lower temperature (cheaper) processing compared to β’’-alumina. Our objective was to identify fundamental structure-processing-property relationships in NaSICON solid electrolytes to inform design for use in sodium batteries. In this work, the mechanical properties of NaSICON sodium ion conductors are affected by sodium conduction. Electrochemical cycling can alter modulus and hardness in NaSICON. Excessive cycling can lead to secondary phases and/or dendrite formation that change mechanical properties in NaSICON. Mechanical and electrochemical properties can be correlated with topographical features to further inform design decisions