Publications

Abstract not provided.

A combination of electrodeposition and thermal reduction methods have been utilized for the synthesis of ligand-free FeNiCo alloy nanoparticles through a high-entropy oxide intermediate. These phases are of great interest to the electrocatalysis community, especially when formed by a sustainable chemistry method. This is successfully achieved by first forming a complex five element amorphous FeNiCoCrMn high-entropy oxide (HEO) phase via electrodeposition from a nanodroplet emulsion solution of the metal salt reactants. The amorphous oxide phase is then thermally treated and reduced at 570-600 °C to form the crystalline FeNiCo alloy with a separate CrMnOx cophase. The FeNiCo alloy is fully characterized by scanning transmission electron microscopy and energy-dispersive X-ray spectroscopy elemental analysis and is identified as a face-centered cubic crystal with the lattice constant a = 3.52 Å. The unoptimized, ligand-free FeNiCo NPs activity toward the oxygen evolution reaction is evaluated in alkaline solution and found to have an ∼185 mV more cathodic onset potential than the Pt metal. Beyond being able to synthesize highly crystalline, ligand-free FeNiCo nanoparticles, the demonstrated and relatively simple two-step process is ideal for the synthesis of tailor-made nanoparticles where the desired composition is not easily achieved with classical solution-based chemistries.

Abstract not provided.

Photon detection at microwave frequency is of great interest due to its application in quantum computation information science and technology. Herein are results from studying microwave response in a topological superconducting quantum interference device (SQUID) realized in Dirac semimetal Cd3As2. The temperature dependence and microwave power dependence of the SQUID junction resistance are studied, from which we obtain an effective temperature at each microwave power level. It is observed the effective temperature increases with the microwave power. This observation of large microwave response may pave the way for single photon detection at the microwave frequency in topological quantum materials.

Formation of zeolite supported Ag0 clusters depends on a combination of thermodynamically stable atomic configurations, charge balance considerations, and mobility of species on the surface and within pores. Periodic density functional theory (DFT) calculations were performed to evaluate how the location of Al in the mordenite (MOR) framework and humidity control Ag0 nanocluster formation. Four Al framework sites were studied (T1-T4) and the Al positions in the framework were identified by the shifts in the differential Al⋯Al pair distribution function (PDF). Furthermore, structural information about the Ag0 nanoclusters, such as dangling bonds, can be identified by Ag⋯Ag PDF data. For Ag0 formation in vacuum MOR structures with a Si:Al ratio of 5:1 with Al in the T1 position resulted in the most framework flexibility and the lowest Ag0 nanocluster charge, indicating the best result for formation of charge neutral nanoclusters. When water is present, Al in the T3 and T4 positions results in the formation of the smallest average Ag0 nanoclusters plus greater expansion of the O-T-O bond angle than in vacuum, indicating easier diffusion of the Ag0 nanoclusters to the surface. The presence of Al in 4-membered rings and in pairs indicates favorable MOR structures for formation of single Ag atoms, despite the existence of synthesis challenges. Therefore, Al in the T2 position is the least favorable for Ag0 nanocluster formation in both vacuum and in the presence of water. Al in the T1, T3, and T4 positions provides beneficial effects through framework flexibility and changes in nanocluster size or charge that can be leveraged for design of zeolites for formation of metallic nanoclusters.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

This report is a functional review of the radionuclide containment strategies of fluoride-salt-cooled high temperature reactor (FHR), molten salt reactor (MSR) and high temperature gas reactor (HTGR) systems. This analysis serves as a starting point for further, more in-depth analyses geared towards identifying phenomenological gaps that still exist, hindering the creation of a mechanistic source term for these reactor types. As background information to this review, an overview of how a mechanistic source term is created and used for consequence assessment necessary for licensing is provided. How a mechanistic source term is used within the Licensing Modernization Project (LMP) is also provided. Lastly, the characteristics of non-LWR mechanistic source terms are examined. This report does not assess the viability of any software system for use with advanced reactor designs, but instead covers system function requirements. Future work within the Nuclear Energy Advanced Modeling and Simulations (NEAMS) program will address such gaps. This document is an update of SAND 2020-6730. An additional chapter is included as well as edits to original content.

This study relates structure, properties and thermodynamics, through synthesis, characterization and heat of formation measurements of rare earth iridate pyrochlore (RE2Ir2O7; RE ​= ​Y, Eu, Pr) crystalline powders. The RE2Ir2O7 phases are synthesized by high temperature solid-state synthesis methods. X-ray diffraction and elemental analysis techniques are utilized to validate the synthesis and enable structural comparisons. Trends in the bond angles indicate deviations from the Y and Eu analogs for the Pr2Ir2O7 phase. High temperature oxide melt solution calorimetry is used to determine the heats of formation of each phase. Breaking the trend expected across the rare earth series, the enthalpy of formation for Pr2Ir2O7 is more exothermic than the anticipated from the Y and Eu analogs.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Reactive gas formation in pores of metal–organic frameworks (MOFs) is a known mechanism of framework destruction; understanding those mechanisms for future durability design is key to next generation adsorbents. Herein, an extensive set of ab initio molecular dynamics (AIMD) simulations are used for the first time to predict competitive adsorption of mixed acid gases (NO2 and H2O) and the in-pore reaction mechanisms for a series of rare earth (RE)-DOBDC MOFs. Spontaneous formation of nitrous acid (HONO) is identified as a result of deprotonation of the MOF organic linker, DOBDC. The unique DOBDC coordination to the metal clusters allows for proton transfer from the linker to the NO2 without the presence of H2O and may be a factor in DOBDC MOF durability. This is a previously unreported mechanisms of HONO formation in MOFs. With the presented methodology, prediction of future gas interactions in new nanoporous materials can be achieved.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Three M-MOF-74 (M = Co, Mg, Ni) metal-organic framework (MOF) thin film membranes have been synthesized through a sensor functionalization method for the direct electrical detection of NO2. The two-step surface functionalization procedure on the glass/Pt interdigitated electrodes resulted in a terminal carboxylate group, with both steps confirmed through infrared spectroscopic analysis. This surface functionalization allowed the MOF materials to grow largely in a uniform manner over the surface of the electrode forming a thin film membrane over the Pt sensing elec-trodes. The growth of each membrane was confirmed through scanning electron microscopy (SEM) and X-ray diffraction analysis. The Ni and Mg MOFs grew as a continuous but non-defect free membrane with overlapping polycrystallites across the glass surface, whereas the Co-MOF-74 grew dis-continuously. To demonstrate the use of these MOF membranes as an NO2 gas sensor, Ni-MOF-74 was chosen as it was consistently fabricated as the best thin and homogenous membrane, as confirmed by SEM. The membrane was exposed to 5 ppm NO2 and the impedance magnitude was observed to decrease 123× in 4 h, with a larger change in impedance and a faster response than the bulk material. Importantly, the use of these membranes as a sensor for NO2 does not require them to be defect-free, but solely continuous and overlapping growth.

Through a combination of single crystal growth, experiments involving in situ deposition of surface adatoms, and complimentary modeling, we examine the electronic transport properties of lithium-decorated ZrTe5 thin films. We observe that the surface states in ZrTe5 are robust against Li adsorption. Both the surface electron density and the associated Berry phase are remarkably robust to adsorption of Li atoms. Fitting to the Hall conductivity data reveals that there exist two types of bulk carriers: those for which the carrier density is insensitive to Li adsorption, and those whose density decreases during initial Li depositions and then saturates with further Li adsorption. We propose this dependence is due to the gating effect of a Li-adsorption-generated dipole layer at the ZrTe5 surface.

Abstract not provided.

Detection and capture of toxic nitrogen oxides (NO_x) is important for emissions control of exhaust gases and general public health. The ability to directly electrically detect trace (0.5–5 ppm) NO₂ by a metal–organic framework (MOF)-74-based sensor at relatively low temperatures (50 °C) is demonstrated via changes in electrical properties of M-MOF-74, M = Co, Mg, Ni. The magnitude of the change is ordered Ni > Co > Mg and explained by each variant's NO₂ adsorption capacity and specific chemical interaction. Ni-MOF-74 provides the highest sensitivity to NO₂; a 725× decrease in resistance at 5 ppm NO2 and detection limit <0.5 ppm, levels relevant for industry and public health. Furthermore, the Ni-MOF-74-based sensor is selective to NO₂ over N₂, SO₂, and air. Linking this fundamental research with future technologies, the high impedance of MOF-74 enables applications requiring a near-zero power sensor or dosimeter, with the active material drawing <15 pW for a macroscale device 35 mm² with 0.8 mg MOF-74. Finally, this represents a 10⁴–10⁶× decrease in power consumption compared to other MOF sensors and demonstrates the potential for MOFs as active components for long-lived, near-zero power chemical sensors in smart industrial systems and the internet of things.

Adsorption of corrosive SO2 gas occurs in metal-organic frameworks (MOFs) including UiO-66. Improvements in SO2 capacity is obtained through the incorporation of residual modulators in the UiO-66 framework by introducing new binding sites in the material, through residual modulators. Four residual modulators were investigated (acetic acid, trifluoroacetic acid, 3-DMAP acid, cyanoacetic acid), and the UiO-66 framework modulated with cyanoacetic acid exhibited nearly twice the SO2 uptake for the 18:1 modulator/linker synthesis ratio compared with other modulated UiO-66 structures. Density functional theory investigations confirmed that targeted host-guest interactions were maintained after the modulator was incorporated into the framework. The strongest binding energy was between SO2 and cyanoacetic acid, consistent with dynamic SO2 adsorption data, and identified contributions from both the SO2 reacting with the residual modulator and the coordinating linkers. The successful increase in dynamic SO2 capacity illustrates how often-overlooked non-covalent interactions can be used in targeted adsorption applications. Further investigation into weak electrostatic interactions for adsorption properties is also needed to advance the potential selectivity and capacity in the adsorption sphere.

Abstract not provided.

Improving predictive models for noble gas transport through natural materials at the field-scale is an essential component of improving US nuclear monitoring capabilities. Several field-scale experiments with a gas transport component have been conducted at the Nevada National Security Site (Non-Proliferation Experiment, Underground Nuclear Explosion Signatures Experiment). However, the models associated with these experiments have not treated zeolite minerals as gas adsorbing phases. This is significant as zeolites are a common alteration mineral with a high abundance at these field sites and are shown here to significantly fractionate noble gases during field-scale transport. This fractionation and associated retardation can complicate gas transport predictions by reducing the signal-to-noise ratio to the detector (e.g. mass spectrometers or radiation detectors) enough to mask the signal or make the data difficult to interpret. Omitting adsorption-related retardation data of noble gases in predictive gas transport models therefore results in systematic errors in model predictions where zeolites are present.Herein is presented noble gas adsorption data collected on zeolitized and non-zeolitized tuff. Experimental results were obtained using a unique piezometric adsorption system designed and built for this study. Data collected were then related to pure-phase mineral analyses conducted on clinoptilolite, mordenite, and quartz. These results quantify the adsorption capacity of materials present in field-scale systems, enabling the modeling of low-permeability rocks as significant sorption reservoirs vital to bulk transport predictions.

Abstract not provided.

This report is a functional review of the radionuclide containment strategies of fluoride-salt-cooled high temperature reactor (FHR), molten salt reactor (IVISR) and high temperature gas reactor (HTGR) systems. This analysis serves as a starting point for further, more in-depth analyses geared towards identifying phenomenological gaps that still exist, preventing the creation of a mechanistic source term for these reactor types. As background information to this review, an overview of how a mechanistic source term is created and used for consequence assessment necessary for licensing is provided. How mechanistic source term is used within the LMP is also provided. Third, the characteristics of non-LWR mechanistic source terms are examined This report does not assess the viability of any software system for use with advanced reactor designs, but instead covers system function requirements. Future work within the Nuclear Energy Advanced Modeling and Simulations (NEAMS) program will address such gaps.

A novel metal-organic framework (MOF), Mn-DOBDC, has been synthesized in an effort to investigate the role of both the metal center and presence of free linker hydroxyls on the luminescent properties of DOBDC (2,5-dihydroxyterephthalic acid) containing MOFs. Co-MOF-74, RE-DOBDC (RE-Eu and Tb), and Mn-DOBDC have been synthesized and analyzed by powder X-ray diffraction (PXRD) and the fluorescent properties probed by UV-Vis spectroscopy and density functional theory (DFT). Mn-DOBDC has been synthesized by a new method involving a concurrent facile reflux synthesis and slow crystallization, resulting in yellow single crystals in monoclinic space group C2/c. Mn-DOBDC was further analyzed by single-crystal X-ray diffraction (SCXRD), scanning electron microscopy-energy-dispersive spectroscopy (SEM-EDS), and photoluminescent emission. Results indicate that the luminescent properties of the DOBDC linker are transferred to the three-dimensional structures of both the RE-DOBDC and Mn-DOBDC, which contain free hydroxyls on the linker. In Co-MOF-74 however, luminescence is quenched in the solid state due to binding of the phenolic hydroxyls within the MOF structure. Mn-DOBDC exhibits a ligand-based tunable emission that can be controlled in solution by the use of different solvents.

The magnetic susceptibility of NOx-loaded RE-DOBDC (rare earth (RE): Y, Eu, Tb, Yb; DOBDC: 2,5-dihydroxyterephthalic acid) metal-organic frameworks (MOFs) is unique to the MOF metal center. RE-DOBDC samples were synthesized, activated, and subsequently exposed to humid NOx. Each NOx-loaded MOF was characterized by powder X-ray diffraction, and the magnetic characteristics were probed by using a VersaLab vibrating sample magnetometer (VSM). Lanthanide-containing RE-DOBDC (Eu, Tb, Yb) are paramagnetic with a reduction in paramagnetism upon adsorption of NOx. Y-DOBDC has a diamagnetic moment with a slight reduction upon adsorption of NOx. The magnetic susceptibility of the MOF is determined by the magnetism imparted by the framework metal center. The electronic population of orbitals contributes to determining the extent of magnetism and change with NOx (electron acceptor) adsorption. Eu-DOBDC results in the largest mass magnetization change upon adsorption of NOx due to more available unpaired f electrons. Experimental changes in magnetic moment were supported by density functional theory (DFT) simulations of NOx adsorbed in lanthanide Eu-DOBDC and transition metal Y-DOBDC MOFs.

Metal-organic frameworks (MOFs) NU-1000 and UiO-66 are herein exposed to two different gamma irradiation doses and dose rates and analyzed to determine the structural features that affect their stability in these environments. MOFs have shown promise for the capture and sensing of off-gases at civilian nuclear energy reprocessing sites, nuclear waste repositories, and nuclear accident locations. However, little is understood about the structural features of MOFs that contribute to their stability levels under the ionizing radiation conditions present at such sites. This study is the first of its kind to explore the structural features of MOFs that contribute to their radiolytic stability. Both NU-1000 and UiO-66 are MOFs that contain Zr metal-centers with the same metal absorption cross section. However, the two MOFs exhibit different linker connectivities, linker aromaticities, node densities, node connectivities, and interligand separations. In this study, NU-1000 and UiO-66 were exposed to high (423.3 Gy/min, 23 min, and 37 s) and low (0.78 Gy/min, 4320 min) dose rates of 60Co gamma irradiation. NU-1000 displayed insignificant radiation damage under both dose rates due to its high linker connectivity, low node density, and low node connectivity. However, low radiation dose rates caused considerable damage to UiO-66, a framework with lower aromaticity and smaller interligand separation. Results suggest that chronic, low-radiation environments are more detrimental to Zr MOF stability than acute, high-radiation conditions.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Zeolite-supported Ag⁰ clusters have broad applications from catalysis to medicine, necessitating a mechanistic understanding of the formation of Ag⁰ clusters in situ. Density functional theory (DFT) simulations have been performed on silver, water, and silver–water clusters in silica mordenite (Si-MOR), to identify the role of the confinement on the structure and energetics of Ag⁰ cluster formation. The most favorable binding energy in the 12-membered ring (MR) pore of the Si-MOR is a 10–15-atom Ag⁰ cluster. Computational pair distribution function (PDF) data indicates that the Ag⁰ and Ag⁰–H₂O clusters formed in vacuum versus in Si-MOR exhibit structural differences. Additionally, when the Ag⁰ cluster is confined, the density decreases and the surface area increases, hypothesized to be due to the limiting geometry of the 12-MR main channel. An energetic drive toward formation of larger Ag⁰ clusters was also identified, with hydrated silver atoms generating higher energy structures. In conclusion, this work identifies mechanistic and structural insight into the role of nanoconfinement on formation of Ag⁰ clusters in mordenite.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Organic linkers in metal-organic framework (MOF) materials exhibit differences in hydrogen bonding (H-bonding), which can alter the geometric, electronic, and optical properties of the MOF. Density functional theory (DFT) simulations were performed on a photoluminescent Y-2,5-dihydroxyterephthalic acid (DOBDC) MOF with H-bonding concentrations between 0 and 100%; the H-bonds were located on both bidentate-and monodentate-bound DOBDC linkers. At 0% H-bond concentration in the framework, the lattice parameters contracted, the density increased, and simulated X-ray diffraction patterns shifted. Comparison with published experimental data identified that Y-DOBDC MOF structures must have a degree of H-bond concentration. The concentration of H-bonds in the system shifted the calculated band gap energy from 2.25 eV at 100% to 3.00 eV at 0%. The band gap energies also indicate a distinction of H-bonds formed on bidentate-coordinated linkers compared to those on monodentate linkers. Additionally, when the calculated optical spectra are compared with experimental data, the ligand-to-ligand charge-transfer luminescence in Y-DOBDC MOFs is expected to result from an average of 20-40% H-bonding with at least 50% of the bidentate linkers containing H-bonding. Therefore, the type of H-bonding within the DOBDC linker determines the electronic structure and the optical absorption of the MOF framework structure. Tuning of the H-bonding in rare-earth MOFs provides an opportunity to control the specific optical and adsorption properties of the MOF framework on the basis of reactions between the linker and the environment.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.