Skyrmions and antiskyrmions are nanoscale swirling textures of magnetic moments formed by chiral interactions between atomic spins in magnetic noncentrosymmetric materials and multilayer films with broken inversion symmetry. These quasiparticles are of interest for use as information carriers in next-generation, low-energy spintronic applications. To develop skyrmion-based memory and logic, we must understand skyrmion-defect interactions with two main goals—determining how skyrmions navigate intrinsic material defects and determining how to engineer disorder for optimal device operation. Here, we introduce a tunable means of creating a skyrmion-antiskyrmion system by engineering the disorder landscape in FeGe using ion irradiation. Specifically, we irradiate epitaxial B20-phase FeGe films with 2.8 MeV Au4+ ions at varying fluences, inducing amorphous regions within the crystalline matrix. Using low-temperature electrical transport and magnetization measurements, we observe a strong topological Hall effect with a double-peak feature that serves as a signature of skyrmions and antiskyrmions. These results are a step towards the development of information storage devices that use skyrmions and antiskyrmions as storage bits, and our system may serve as a testbed for theoretically predicted phenomena in skyrmion-antiskyrmion crystals.
An in situ ion irradiation scanning electron microscope (I3SEM) has been developed, installed, and integrated into the Ion Beam Laboratory at Sandia National Laboratories. The I3SEM facility combines a field emission, variable pressure, scanning electron microscope, a 6 MV tandem accelerator, high flux low energy ion source, an 808 nm-wavelength laser, and multiple stages to control the thermal and mechanical state of the sample observed. The facility advances real-time understanding of materials evolution under combined environments at the mesoscale. As highlighted in multiple examples, this unique combination of tools is optimized for studying mesoscale material response in overlapping extreme environments, allowing for simultaneous ion irradiation, implantation, laser bombardment, conductive heating, cooling, and mechanical deformation.
High‐Entropy Alloys (HEAs) are proposed as materials for a variety of extreme environments, including both fission and fusion radiation applications. To withstand these harsh environments, materials processing must be tailored to their given application, now achieved through additive manufacturing processes. However, radiation application opportunities remain limited due to an incomplete understanding of the effects of irradiation on HEA performance. In this letter, we investigate the response of additively manufactured refractory high‐entropy alloys (RHEAs) to helium (He) ion bombardment. Through analytical microscopy studies, we show the interplay between the alloy composition and the He bubble size and density to demonstrate how increasing the compositional complexity can limit the He bubble effects, but care must be taken in selecting the appropriate constituent elements.
The dynamic interactions of ions with matter drive a host of complex evolution mechanisms, requiring monitoring on short spatial and temporal scales to gain a full picture of a material response. Understanding the evolution of materials under ion irradiation and displacement damage is vital for many fields, including semiconductor processing, nuclear reactors, and space systems. Despite materials in service having a dynamic response to radiation damage, typical characterization is performed post-irradiation, washing out all information from transient processes. Characterizing active processes in situ during irradiation allows the mechanisms at play during the dynamic ion-material interaction process to be deciphered. In this review, we examine the in situ characterization techniques utilized for examining material structure, composition, and property evolution under ion irradiation. Covering analyses of microstructure, surface composition, and material properties, this work offers a perspective on the recent advances in methods for in situ monitoring of materials under ion irradiation, including a future outlook examining the role of complementary and combined characterization techniques in understanding dynamic materials evolution.
Metal hydrides can store hydrogen isotopes with high volumetric density. In metal tritides, tritium beta decay can result in accumulation of helium within the solid, in some cases exceeding 10 at.% helium after only 4 years of aging. Helium is insoluble in most materials, but often does not readily escape, and instead coalesces to form nanoscale bubbles when helium concentrations are near 1 at.%. Blistering or spallation often occurs at higher concentrations. Radioactive particles shed during this process present a potential safety hazard. This study investigates the effects of high helium concentrations on erbium deuteride (ErD2), a non-radioactive surrogate material for erbium tritide (ErT2). To simulate tritium decay in the surrogate, high doses of 120 keV helium ions were implanted into ErD2 films at room temperature. Scanning and transmission electron microscopy indicated spherical helium bubble formation at a critical concentration of 1.5 at.% and bubble linkage leading to nanoscale crack formation at a concentration of 7.5 at.%. Additionally, crack propagation occurred through the nanocrack region, resulting in spallation extending from the implantation peak to the surface. Electron energy loss spectroscopy was utilized to confirm the presence of high-pressure helium in the nanocracks, suggesting that helium gas plays a predominant role in deformation. This work improves the overall understanding of helium behavior in ErD2 by using modern characterization techniques to determine: the critical helium concentration required for bubble formation, the material failure mechanism at high concentration, and the nanoscale mechanisms responsible for material failure in helium implanted ErD2.
A synthesis process is presented for experimentally simulating modifications in cosmic dust grains using sequential ion implantations or irradiations followed by thermal annealing. Cosmic silicate dust analogues were prepared via implantation of 20–80 keV Fe−, Mg−, and O− ions into commercially available p-type silicon (100) wafers. The as-implanted analogues are amorphous with a Mg/(Fe + Mg) ratio of 0.5 tailored to match theoretical abundances in circumstellar dusts. Before the ion implantations were performed, Monte-Carlo-based ion-solid interaction codes were used to model the dynamic redistribution of the implanted atoms in the silicon substrate. 600 keV helium ion irradiation was performed on one of the samples before thermal annealing. Two samples were thermally annealed at a temperature appropriate for an M-class stellar wind, 1000 K, for 8.3 h in a vacuum chamber with a pressure of 1 × 10−7 torr. The elemental depth profiles were extracted utilizing Rutherford Backscattering Spectrometry (RBS) in the samples before and after thermal annealing. X-ray diffraction (XRD) analysis was employed for the identification of various phases in crystalline minerals in the annealed analogues. Transmission electron microscopy (TEM) analysis was utilized to identify specific crystal structures. RBS analysis shows redistribution of the implanted Fe, Mg, and O after thermal annealing due to incorporation into the crystal structures for each sample type. XRD patterns along with TEM analysis showed nanocrystalline Mg and Fe oxides with possible incorporation of additional silicate minerals.
Stainless steel TPBAR components undergo neutron radiation-induced segregation and dislocation loop formation. Comparison experiments with ion beams accelerate the damage, and visualize the damage process with in-situ microscopy. In-situ Au irradiation causes defect formation, but no elemental segregation.