Electrodeposition of a High Magnetostriction CoFe Film

Journal of the Electrochemical Society

Pillars, Jamin R.; Langlois, Eric L.; Arrington, Christian L.; Monson, Todd M.; Hollowell, Andrew E.; Rodriguez, Mark A.

The development of an electrodeposition process for cobalt/iron (CoFe) alloys with minimal oxygen concentration and controlled stoichiometry is necessary for the advancement of magnetostrictive device functionalities. CoFe alloy films were electrodeposited out of a novel chemistry onto copper test structures enabling magnetic displacement testing for magnetostriction calculations. Using a combination of additives that served as oxygen scavengers, grain refiners, and complexing agents in conjunction with a pulsed plating technique, CoFe films were synthesized at thicknesses as high as 10μm with less than 8 at% oxygen at a stoichiometry of 70-75% Co and 25-30% Fe. X-Ray diffraction (XRD) analysis confirmed that these films had a crystal structure consistent with 70% Co 30% Fe Wairuaite with a slight lattice contraction due to Co doping in the film. A novel characterization technique was used to measure the displacement of the CoFe films electrodeposited, as a function of applied magnetic bias, in order to determine the saturation magnetostriction (λS) of the material. With this chemistry and a tailored pulse plating regime, λS values as high as 172 ± 25ppm have been achieved. This is believed by the authors to be the highest reported value of magnetostriction for an electrodeposited CoFe film.

More Details
TYPE Journal Article YEAR 2015
OSTIOSTI
Results 51–75 of 95
Results 51–75 of 95