We describe a correlation between electrical resistivity and grain size for PVD synthesized polycrystalline oxide-hardened metal-matrix thin films in oxide-dilute (<5 vol. % oxide phase) compositions. The correlation is based on the Mayadas-Shatzkes (M-S) electron scattering model, predictive of grain size evolution as a function of composition in the oxide-dilute regime for 2 μm thick Au-ZnO films. We describe a technique to investigate grain boundary (GB) mobility and the thermal stability of GBs based on in situelectrical resistivity measurements during annealing experiments, interpreted using a combination of the M-S model and the Michels et al. model describing solute drag stabilized grain growth kinetics. Using this technique, activation energy and pre-exponential Arrhenius parameter values of Ea = 21.6 kJ/mol and Ao = 2.3 × 10-17 m2/s for Au-1 vol. % ZnO and Ea =12.7 kJ/mol and Ao = 3.1 × 10-18 m2/s for Au-2 vol.% ZnO were determined. In the oxide-dilute regime, the grain size reduction of the Au matrix yielded a maximum hardness of 2.6 GPa for 5 vol. % ZnO. A combined model including percolation behavior and grain refinement is presented that accurately describes the composition dependent change in electrical resistivity throughout the entire composition range for Au-ZnO thin films. As a result, the proposed correlations are supported by microstructural characterization using transmission electron microscopy and electron diffraction mapping for grain size determination.
Dynamic control of thermal transport in solid-state systems is a transformative capability with the promise to propel technologies including phononic logic, thermal management, and energy harvesting. A solid-state solution to rapidly manipulate phonons has escaped the scientific community. We demonstrate active and reversible tuning of thermal conductivity by manipulating the nanoscale ferroelastic domain structure of a Pb(Zr0.3Ti0.7)O3 film with applied electric fields. With subsecond response times, the room-temperature thermal conductivity was modulated by 11%.
This report provides a detailed characterization Tri-lab Tantalum (Ta) plate jointly purchased from HCStark Inc. by Sandia, Los Alamos and Lawrence Livermore National Laboratories. Data in this report was compiled from series of material and properties characterization experiments carried out at Sandia (SNL) and Los Alamos (LANL) Laboratories through a leveraged effort funded by the C2 campaign. Results include microstructure characterization detailing the crystallographic texture of the material and an increase in grain size near the end of the rolled plate. Mechanical properties evaluations include, compression cylinder, sub-scale tension specimen, micohardness and instrumented indentation testing. The plate was found to have vastly superior uniformity when compare with previously characterized wrought Ta material. Small but measurable variations in microstructure and properties were noted at the end, and at the top and bottom edges of the plate.