This progress report describes work performed during FY22 at Sandia National Laboratories (SNL) to assess the corrosion performance of cold spray coatings to enable optimization of cold spray for the purposes of mitigation and/or repair of potentially susceptible regions, corrosion, or stress corrosion cracking (SCC) in austenitic stainless steel for spent nuclear fuel (SNF) storage. Of particular concern is SCC, by which a through-wall crack could potentially form in a canister outer wall over time intervals that may be shorter than possible dry storage times. In FY21, initial corrosion explorations of cold spray coating were evaluated and in FY22, an expanded set of cold spray coatings with in-depth analysis of post-exposure accelerated testing was explored. Additionally, relevant atmospheric exposure testing was carried out and initial results are presented herein. The corrosion attack from the accelerated testing and more realistic atmospheric exposures environments were compared to identify potentially deleterious factors for corrosion as well as help to understand the applicability of accelerated testing for cold spray optimization. This initial analysis will help to enable optimization of the corrosion resistance cold spray, one of the more promising coating and repair techniques, for potential application in an SNF environment. Learnings from both are summarized, and implications and future work are presented in this report.

The chloride-induced stress corrosion cracking (CISCC) mechanism of cold spray (CS) coating on a galvanically similar substrate is investigated. Arc welded 304L stainless steel (SS) specimens are loaded into four-point bend fixtures, cold sprayed with 304L SS, then immersed in boiling MgCl2. Interconnected porosity forms through crevice corrosion along CS splat boundaries, allowing corrosive species to penetrate through the CS layer. Nevertheless, the substrate is resistant to CISCC likely because of compressive stress introduced by peening during CS particle impacts. These findings underscore the importance of residual stress in the environmental degradation of CS coatings or repairs of engineering structures.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Residual stress is a contributor to stress corrosion cracking (SCC) and a common byproduct of additive manufacturing (AM). Here the relationship between residual stress and SCC susceptibility in laser powder bed fusion AM 316L stainless steel was studied through immersion in saturated boiling magnesium chloride per ASTM G36-94. The residual stress was varied by changing the sample height for the as-built condition and additionally by heat treatments at 600°C, 800°C, and 1,200°C to control, and in some cases reduce, residual stress. In general, all samples in the as-built condition showed susceptibility to SCC with the thinner, lower residual stress samples showing shallower cracks and crack propagation occurring perpendicular to melt tracks due to local residual stress fields. The heat-treated samples showed a reduction in residual stress for the 800°C and 1,200°C samples. Both were free of cracks after >300 h of immersion in MgCl2, while the 600°C sample showed similar cracking to their as-built counterpart. Geometrically necessary dislocation (GND) density analysis indicates that the dislocation density may play a major role in the SCC susceptibility.

Abstract not provided.

Additively manufactured (AM) stainless steels (SSs) exhibit numerous microstructural differences compared to their wrought counterparts, such as Cr-enriched dislocation cell structures. The influence these unique features have on a SSs corrosion resistance are still under investigation with most current works limited to laboratory experiments. The work herein shows the first documented study of AM 304L and 316L exposed to a severe marine environment on the eastern coast of Florida with comparisons made to wrought counterparts. Coupons were exposed for 21 months and resulted in significant pitting corrosion to initiate after 1 month of exposure for all conditions. At all times, the AM coupons exhibited lower average and maximum pit depths than their wrought counterparts. After 21 months, pits on average were 4 μm deep for AM 316L specimen and 8 μm deep for wrought specimen. Pits on the wrought samples tended to be nearly hemispherical and polished with some pits showing crystallographic attack while pits on AM coupons exhibited preferential attack at melt pool boundaries and the cellular microstructure.