A series of compaction experiments was conducted to evaluate the mechanical, reactive, and deflagration-to-detonation transition behavior in Alliant Bullseye powder. Using a novel application of photonic Doppler velocimetry and light fibers, the experiments measured both compaction and combustion waves in porous beds of Bullseye subjected to impact by gun-driven pistons. Relationships between initial piston velocity and transition distance are shown. Comparison is made between the Bullseye response and that found in classic Type I DDT.
Experiments on the Sandia Z pulsed-power accelerator have demonstrated the ability to produce warm dense matter (WDM) states with unprecedented uniformity, duration, and size, which are ideal for investigations of fundamental WDM properties. For the first time, space-resolved x-ray Thomson scattering (XRTS) spectra from shocked carbon foams were recorded on Z. The large (>20 MA) electrical current produced by Z was used to launch Al flyer plates up to 25 km/s. The impact of the flyer plate on a CH2 foam target produced a shocked state with an estimated pressure of 0.75 Mbar, density of 0.52 g/cm3, and temperature of 4.3 eV. Both unshocked and shocked portions of the foam target were probed with 6.2 keV x-rays produced by focusing the Z-Beamlet laser onto a nearby Mn foil. The data are composed of three spatially distinct spectra that were simultaneously captured with a single spectrometer with high spectral (4.8 eV) and spatial (190 μm) resolutions. Detailed spectral information from three target locations is provided simultaneously: the incident x-ray source, the scattered signal from unshocked foam, and the scattered signal from shocked foam.
We report on experiments where cylindrical beryllium liners filled with liquid deuterium were compressed to extreme pressure and density with current pulse shaping. In one set of experiments the pressure at stagnation is inferred to be & 100 Mbar using penetrating radiography. A peak liner convergence ratio (initial radius over final radius) of 7.6 was measured resulting in an average deuterium density of 10 g=cm3 and areal density of 0.45 g=cm2. The stagnation shock propagating radially outward through the liner wall was directly measured with a strength of ≈ 120 Mbar. In a second set of experiments the liner was imploded to a peak convergence of 19 resulting in a density of 55 g=cm3 and areal density of 0.5 g=cm2. The pressure at stagnation in this experiment is estimated to be 2 Gbar. This platform enables the study of high-pressure, high-density, implosion deceleration and stagnation dynamics at spatial scales that are readily diagnosable (R ~ 0.1 -- 0.4 mm). Thus, these experiments are directly relevant to both Inertial Con nement Fusion and the study of material properties under extreme conditions.