Residual stress is a common result of manufacturing processes, but it is one that is often overlooked in design and qualification activities. There are many reasons for this oversight, such as lack of observable indicators and difficulty in measurement. Traditional relaxation-based measurement methods use some type of material removal to cause surface displacements, which can then be used to solve for the residual stresses relieved by the removal. While widely used, these methods may offer only individual stress components or may be limited by part or cut geometry requirements. Diffraction-based methods, such as X-ray or neutron, offer non-destructive results but require access to a radiation source. With the goal of producing a more flexible solution, this LDRD developed a generalized residual stress inversion technique that can recover residual stresses released by all traction components on a cut surface, with much greater freedom in part geometry and cut location. The developed method has been successfully demonstrated on both synthetic and experimental data. The project also investigated dislocation density quantification using nonlinear ultrasound, residual stress measurement using Electronic Speckle Pattern Interferometry Hole Drilling, and validation of residual stress predictions in Additive Manufacturing process models.

Intermetallic alloys possess exceptional soft magnetic properties, including high permeability, low coercivity, and high saturation induction, but exhibit poor mechanical properties that make them impractical to bulk process and use at ideal compositions. We used laser-based Additive Manufacturing to process traditionally brittle Fe–Co and Fe–Si alloys in bulk form without macroscopic defects and at near-ideal compositions for electromagnetic applications. The binary Fe–50Co, as a model material, demonstrated simultaneous high strength (600–700 MPa) and high ductility (35%) in tension, corresponding to a ∼300% increase in strength and an order-of-magnitude improvement in ductility relative to conventionally processed material. Atomic-scale toughening and strengthening mechanisms, based on engineered multiscale microstructures, are proposed to explain the unusual combination of mechanical properties. This work presents an instance in which metal Additive Manufacturing processes are enabling, rather than limiting, the development of higher-performance alloys.

This study investigates the mechanical and corrosion properties of as-built and annealed equiatomic CoCrFeMnNi alloy produced by laser-based directed energy deposition (DED) Additive Manufacturing (AM). The high cooling rates of DED produced a single-phase, cellular microstructure with cells on the order of 4 μm in diameter and inter-cellular regions that were enriched in Mn and Ni. Annealing created a chemically homogeneous recrystallized microstructure with a high density of annealing twins. The average yield strength of the as-built condition was 424 MPa and exceeded the annealed condition (232 MPa), however; the strain hardening rate was lower for the as-built material stemming from higher dislocation density associated with DED parts and the fine cell size. In general, the yield strength, ultimate tensile strength, and elongation-to-failure for the as-built material exceeded values from previous studies that explored other AM techniques to produce the CoCrFeMnNi alloy. Ductile fracture occurred for all specimens with dimple initiation associated with nanoscale oxide inclusions. The breakdown potential (onset of pitting corrosion) was similar for the as-built and annealed conditions at 0.40 VAg/AgCl when immersed in 0.6 M NaCl. Pit morphology/propagation for the as-built condition exhibited preferential corrosion of inter-cellular Ni/Mn regions leading to a tortuous pit bottom and cover, while the annealed conditions pits resembled lacy pits similar to 304 L steel. A passive oxide film depleted in Cr cations with substantial incorporation of Mn cations is proposed as the primary mechanism for local corrosion susceptibility of the CoCrFeMnNi alloy.

Abstract not provided.

Abstract not provided.

Control of the atomic structure, as measured by the extent of the embrittling B2 chemically ordered phase, is demonstrated in intermetallic alloys through additive manufacturing (AM) and characterized using high fidelity neutron diffraction. As a layer-by-layer rapid solidification process, AM was employed to suppress the extent of chemically ordered B2 phases in a soft ferromagnetic Fe-Co alloy, as a model material system of interest to electromagnetic applications. The extent of atomic ordering was found to be insensitive to the spatial location within specimens and suggests that the thermal conditions within only a few AM layers were most influential in controlling the microstructure, in agreement with the predictions from a thermal model for welding. Analysis of process parameter effects on ordering found that suppression of B2 phase was the result of an increased average cooling rate during processing. AM processing parameters, namely interlayer interval time and build velocity, were used to systematically control the relative fraction of ordered B2 phase in specimens from 0.49 to 0.72. Hardness of AM specimens was more than 150% higher than conventionally processed bulk material. Implications for tailoring microstructures of intermetallic alloys are discussed.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

This report summarizes the data analysis activities that were performed under the Born Qualified Grand Challenge Project from 2016 - 2018. It is meant to document the characterization of additively manufactured parts and processe s for this project as well as demonstrate and identify further analyses and data science that could be done relating material processes to microstructure to properties to performance.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.