A capability for measuring the thermal conductivity of microelectromechanical systems (MEMS) materials using a steady state resistance technique was developed and used to measure the thermal conductivities of SUMMiT{trademark} V layers. Thermal conductivities were measured over two temperature ranges: 100K to 350K and 293K to 575K in order to generate two data sets. The steady state resistance technique uses surface micromachined bridge structures fabricated using the standard SUMMiT fabrication process. Electrical resistance and resistivity data are reported for poly1-poly2 laminate, poly2, poly3, and poly4 polysilicon structural layers in the SUMMiT process from 83K to 575K. Thermal conductivity measurements for these polysilicon layers demonstrate for the first time that the thermal conductivity is a function of the particular SUMMiT layer. Also, the poly2 layer has a different variation in thermal conductivity as the temperature is decreased than the poly1-poly2 laminate, poly3, and poly4 layers. As the temperature increases above room temperature, the difference in thermal conductivity between the layers decreases.
We describe a Laboratory Directed Research and Development (LDRD) effort to develop and apply laser-based thermometry diagnostics for obtaining spatially resolved temperature maps on working microelectromechanical systems (MEMS). The goal of the effort was to cultivate diagnostic approaches that could adequately resolve the extremely fine MEMS device features, required no modifications to MEMS device design, and which did not perturb the delicate operation of these extremely small devices. Two optical diagnostics were used in this study: microscale Raman spectroscopy and microscale thermoreflectance. Both methods use a low-energy, nonperturbing probe laser beam, whose arbitrary wavelength can be selected for a diffraction-limited focus that meets the need for micron-scale spatial resolution. Raman is exploited most frequently, as this technique provides a simple and unambiguous measure of the absolute device temperature for most any MEMS semiconductor or insulator material under steady state operation. Temperatures are obtained from the spectral position and width of readily isolated peaks in the measured Raman spectra with a maximum uncertainty near {+-}10 K and a spatial resolution of about 1 micron. Application of the Raman technique is demonstrated for V-shaped and flexure-style polycrystalline silicon electrothermal actuators, and for a GaN high-electron-mobility transistor. The potential of the Raman technique for simultaneous measurement of temperature and in-plane stress in silicon MEMS is also demonstrated and future Raman-variant diagnostics for ultra spatio-temporal resolution probing are discussed. Microscale thermoreflectance has been developed as a complement for the primary Raman diagnostic. Thermoreflectance exploits the small-but-measurable temperature dependence of surface optical reflectivity for diagnostic purposes. The temperature-dependent reflectance behavior of bulk silicon, SUMMiT-V polycrystalline silicon films and metal surfaces is presented. The results for bulk silicon are applied to silicon-on-insulator (SOI) fabricated actuators, where measured temperatures with a maximum uncertainty near {+-}9 K, and 0.75-micron inplane spatial resolution, are achieved for the reflectance-based measurements. Reflectance-based temperatures are found to be in good agreement with Raman-measured temperatures from the same device.
The response of microsystem components to laser irradiation is relevant to the use of laser processing, optical diagnostics, and optical microelectromechanical systems (MEMS) device design and performance. The dimensions of MEMS are on the same order as infrared laser wavelengths which results in interference phenomena when the parts are partially transparent. Four distinct polycrystalline structures were designed and irradiated with 808 nm laser light to determine the effect of layers and the presence of a substrate via on the laser power threshold for damage. The presence of a substrate via resulted in lower damage thresholds, and interference phenomena resulted in a single layer structure having the highest damage threshold.
Optical microswitches are being developed for use in communication and security systems because of their small size and fast response time. However, as the intensity of the light incident on the microswitches increases, the thermal and mechanical responses of the reflective surfaces are becoming a concern. It is important to dissipate heat adequately and to minimize any deformation on the reflective surfaces. To understand the mechanical responses of these microswitches, a set of microstructures have been fabricated and tested to evaluate how the surfaces deform when irradiated with a high-intensity laser beam. To evaluate and further investigate the experimental findings, the coupled physical analysis tool, Calagio, has been applied to simulate the mechanical behavior of these test structures when they are optically heated. Code prediction of the surface displacement will be compared against measurement. Our main objective is to assess the existing material models and our code predictive capability so that it will be used to qualify the performance of microswitches being developed.
Microsystems are potentially exposed to laser irradiation during processing, diagnostic measurements, and, in some cases, device operation. The behavior of the components in an optical MEMS device that are irradiated by a laser needs to be optimized for reliable operation. Utilizing numerical simulations facilitates design and optimization. This paper reports on experimental and numerical investigations of the thermomechanical response of polycrystalline silicon microcantilevers that are 250 {micro}m wide, 500 {micro}m long, and 2.25 {micro}m thick when heated by an 808 nm laser. At laser powers above 400 mW significant deflection is observed during the laser pulse using a white light interferometer. Permanent deformation is detected at laser powers above 650 mW in the experiments. Numerical calculations using a coupled physics finite element code, Calagio, agree qualitatively with the experimental results. Both the experimental and numerical results reveal that the initial stress state is very significant. Microcantilevers deflect in the direction of their initial deformation upon irradiation with a laser.
Optical actuation of microelectromechanical systems (MEMS) is advantageous for applications for which electrical isolation is desired. Thirty-two polycrystalline silicon opto-thermal actuators, optically-powered MEMS thermal actuators, were designed, fabricated, and tested. The design of the opto-thermal actuators consists of a target for laser illumination suspended between angled legs that expand when heated, providing the displacement and force output. While the amount of displacement observed for the opto-thermal actuators was fairly uniform for the actuators, the amount of damage resulting from the laser heating ranged from essentially no damage to significant amounts of damage on the target. The likelihood of damage depended on the target design with two of the four target designs being more susceptible to damage. Failure analysis of damaged targets revealed the extent and depth of the damage.
Proceedings of the ASME/Pacific Rim Technical Conference and Exhibition on Integration and Packaging of MEMS, NEMS, and Electronic Systems: Advances in Electronic Packaging 2005