Growth and Fabrication of GaN/AlGaN Heterojunction Bipolar Transistor
A GaN/AlGaN heterojunction bipolar transistor structure with Mg doping in the base and Si Doping in the emitter and collector regions was grown by Metal Organic Chemical Vapor Deposition in c-axis Al(2)O(3). Secondary Ion Mass Spectrometry measurements showed no increase in the O concentration (2-3x10(18) cm(-3)) in the AlGaN emitter and fairly low levels of C (~4-5x10(17) cm (-3)) throughout the structure. Due to the non-ohmic behavior of the base contact at room temperature, the current gain of large area (~90 um diameter) devices was <3. Increasing the device operating temperature led to higher ionization fractions of the mg acceptors in the base, and current gains of ~10 were obtained at 300 degree C.