Current transport in W and WSI{sub x} ohmic contacts to InGaN and InN
The temperature dependence of the specific contact resistance of W and WSi{sub 0.44} contacts on n{sup +} In{sub 0.65}Ga{sub 0.35}N and InN was measured in the range -50 {degrees}C to 125 {degrees}C. The results were compared to theoretical values for different conduction mechanisms, to further elucidate the conduction mechanism in these contact schemes for all but as-deposited metal to InN where thermionic emission appears to be the dominant mechanism. The contacts were found to produce low specific resistance ohmic contacts to InGaN at room temperature, e{sup c} {approximately} 10{sup -7} {Omega} {center_dot} cm{sup 2} for W and e{sub c} of 4x 10{sup -7} {Omega} {center_dot} cm{sup 2} for WSi{sub x}. InN metallized with W produced ohmic contacts with e{sub c} {approximately} 10{sup -7} {Omega} {center_dot} cm{sup 2} and e{sub c} {approximately} 10{sup -6} {Omega} {center_dot} cm{sup 2} for WSi{sub x} at room temperature.