Publications

Abstract not provided.

Abstract not provided.

The lower limit of metal hydride nanoconfinement is demonstrated through the coordination of a molecular hydride species to binding sites inside the pores of a metal-organic framework (MOF). Magnesium borohydride, which has a high hydrogen capacity, is incorporated into the pores of UiO-67bpy (Zr6O4(OH)4(bpydc)6 with bpydc2- = 2,2′-bipyridine-5,5′-dicarboxylate) by solvent impregnation. The MOF retained its long-range order, and transmission electron microscopy and elemental mapping confirmed the retention of the crystal morphology and revealed a homogeneous distribution of the hydride within the MOF host. Notably, the B-, N-, and Mg-edge XAS data confirm the coordination of Mg(II) to the N atoms of the chelating bipyridine groups. In situ 11B MAS NMR studies helped elucidate the reaction mechanism and revealed that complete hydrogen release from Mg(BH4)2 occurs as low as 200 °C. Sieverts and thermogravimetric measurements indicate an increase in the rate of hydrogen release, with the onset of hydrogen desorption as low as 120 °C, which is approximately 150 °C lower than that of the bulk material. Furthermore, density functional theory calculations support the improved dehydrogenation properties and confirm the drastically lower activation energy for B-H bond dissociation.

Abstract not provided.

The thermodynamic stability and melting point of magnesium borohydride were probed under hydrogen pressures up to 1000 bar (100 MPa) and temperatures up to 400 °C. At 400 °C, Mg(BH4)2 was found to be chemically stable between 700 and 1000 bar H2, whereas under 350 bar H2 or lower pressures, the bulk material partially decomposed into MgH2 and MgB12H12. The melting point of solvent-free Mg(BH4)2 was estimated to be 367-375 °C, which was above previously reported values by 40-90 °C. Our results indicated that a high hydrogen backpressure is needed to prevent the decomposition of Mg(BH4)2 before measuring the melting point and that molten Mg(BH4)2 can exist as a stable liquid phase between 367 and 400 °C under hydrogen overpressures of 700 bar or above. The occurrence of a pure molten Mg(BH4)2 phase enabled efficient melt-infiltration of Mg(BH4)2 into the pores of porous templated carbons (CMK-3 and CMK-8) and graphene aerogels. Both transmission electron microscopy and small-angle X-ray scattering confirmed efficient incorporation of the borohydride into the carbon pores. The Mg(BH4)2@carbon samples exhibited comparable hydrogen capacities to bulk Mg(BH4)2 upon desorption up to 390 °C based on the mass of the active component; the onset of hydrogen release was reduced by 15-25 °C compared to the bulk. Importantly, melt-infiltration under hydrogen pressure was shown to be an efficient way to introduce metal borohydrides into the pores of carbon-based materials, helping to prevent particle agglomeration and formation of stable closo-polyborate byproducts.

Complex metal hydrides provide high-density hydrogen storage, which is essential for vehicular applications. However, the practical application of these materials is limited by thermodynamic and kinetic barriers present during the dehydrogenation and rehydrogenation processes as new phases form inside parent phases. An improved understanding of the mixed-phase mesostructures and their interfaces will assist in improving cyclability. In this work, the phase evolution during hydrogenation of lithium nitride and dehydrogenation of lithium amide with lithium hydride is probed with scanning transmission X-ray microscopy at the nitrogen K edge. With this technique, core–shell structures are observed in particles of both partially hydrogenated Li3N and partially dehydrogenated LiNH2 + 2LiH. To generate these structures, the rate-limiting step must shift from internal hydrogen diffusion during hydrogenation to the formation of hydrogen gas at the surface during desorption.