Publications Details
The effect of microstructure on the thermal fatigue resistance of investment cast and wrought AISI H13 hot work die steel
Variable thickness plate investment castings of AISI H13 hot work die steel were pour and characterized in the as-cast and heat treated conditions. The characterization included light microscopy and mechanical testing. Wrought samples of standard and premium grade H13 steel were heat treated and characterized similarly for comparison. Microstructural differences were observed in as-cast samples poured to different section thicknesses. Dendrite cell size and carbide morphology constituted the most prominent microstructural differences observed. After a full heat treatment, however, Microstructural differences between the wrought material and cast materials were slight regardless of section thickness. The mechanical properties of the cast and heat treated material proved similar to the properties of the standard heat treated wrought material. A thermal fatigue testing unit was designed and built to correlate the heat checking susceptibility of AISI H13 steel to its processing and consequent microstructural condition. Surface hardness decreased significantly with thermal cycling, and heat checking was noticed in as few as 50 cycles. Thermal softening and thermal fatigue susceptibility were quantified and discussed relative to the microstructural conditions created by processing and heat treatment. It was found that the premium grade wrought H13 steel provided the best overall resistance to heat checking; however, the heat-treat cast and as-cast H13 tool steel (made from standard grade wrought H13 tool steel) provided comparable resistance to heat checking in terms Of area fraction of heat checking and maximum crack length.