Surface chemistry of MoS{sub 2} lubricant films: 1, Effects of high humidity storage on sputtered films
Many MoS{sub 2} lubricant film formulations exhibit tribological performance degradation after extended storage in high humidity ambient environments. As a part of an extensive study of the effects of high humidity storage on a wide variety of MoS{sub 2} lubricant film formulations, the effects of high humidity storage on sputtered MoS{sub 2} films have been examined. The surface chemistries of a series of ten different commercially deposited MoS{sub 2} lubricant film formulations on 440C stainless steel have been examined before and after 1 month of storage at 98% relative humidity. While the films varied greatly in film chemistry prior to high humidity storage, many smaller differences were observed after high humidity storage. Addition of Ni to the films affects the film chemistry far more dramatically than the addition of AuPd or SbO{sub x}, facilitating oxidation of the MoS{sub 2} and enhancing formation of sulfate species. All of the films are adequately characterized by considering only MoS{sub 2} and MoO{sub 3} species, with the exception of the films co-sputtered with Ni and ion implanted with N{sup +}, where some MoO{sub 2} or MoS{sub 2-x}O{sub x} must also be present.