Reciprocal space analysis of the initial stages of strain relaxation in SiGe epilayers
Metastable SiGe films were grown by MBE on Si (001) substrates and annealed to promote varying degrees of partial relaxation. X-ray diffraction reciprocal-space analysis was then used to monitor the structural evolution of the displacement fields of the dislocation array with increasing misfit density. The diffuse-x-ray-scattering patterns of the dislocated heterolayers were compared with lineal-misfit densities determined by defect etching, leading us to develop a geometric model which provides a framework for understanding the early-stage evolution of the displacement fields of the dislocation array, and which also explicitly links diffuse x-ray intensity to misfit density. At low misfit density, the diffuse intensity arises from two-dimensional displacement fields associated with single-nonoverlapping dislocations. As misfit density increases, the displacement fields of individual dislocations increasingly overlap producing three-dimensional displacements. The evolving diffuse intensity reflects the transition from 2-D to 3-D displacement fields. Finally, it is demonstrated that the diffuse x-ray intensity of the strained epilayer can be used to accurately measure lineal misfit-dislocation densities from 400 to 20,000 lines/cm.