Pulsed ion beam surface treatment for preparing rapidly solidified corrosion resistant steel and aluminum surfaces

Buchheit, R.G.; Maestas, L.M.; Mcintyre, D.C.; Stinnett, R.W.; Greenly, J.B.

Intense, pulsed ion beams were used to melt and rapidly resolidify Types 316F, 316L and sensitized 304 stainless steel surfaces to eliminate the negative effects of microstructural heterogeneity on localized corrosion resistance. Anodic polarization curves determined for 316F and 316L showed that passive current densities were reduced and pitting potentials were increased due to ion beam treatment. Type 304 samples sensitized at 600°C for 100 h showed no evidence of grain boundary attack when surfaces were ion beam treated. Equivalent ion beam treatments were conducted with a 6061-T6 aluminum alloy. Electrochemical impedance experiments conducted with this alloy exposed to an aerated chloride solution showed that the onset of pitting was delayed compared to untreated control samples.