Implantation activation annealing of Si-implanted gallium nitride at temperatures > 1,100 C

Zolper, J.C.

The activation annealing of Si-implanted GaN is reported for temperatures from 1,100 to 1,400 C. Although previous work has shown that Si-implanted GaN can be activated by a rapid thermal annealing at {approximately}1,100 C, it was also shown that significant damage remained in the crystal. Therefore, both AlN-encapsulated and uncapped Si-implanted GaN samples were annealed in a metal organic chemical vapor deposition system in a N{sub 2}/NH{sub 3} ambient to further assess the annealing process. Electrical Hall characterization shows increases in carrier density and mobility for annealing up to 1,300 C before degrading at 1,400 C due to decomposition of the GaN epilayer. Rutherford backscattering spectra show that the high annealing temperatures reduce the implantation induced damage profile but do not completely restore the as-grown crystallinity.