Ferroelectric potassium niobate thin films
We report on the first ferroelectric measurements of chemically prepared KNbO/sub 3/ thin films. Polycrystalline KNbO/sub 3/ thin films were fabricated by dip coating substrates with methanolic solutions of potassium hydroxide and niobium ethoxide. Perovskite KNbO/sub 3/ was obtained for both bulk gels and films by using 800/degree/C firing treatments. For films, the intermediate temperature processing schedule was critical for the complete conversion of low temperature phases to perovskite KNbO/sub 3/. Raman spectroscopy and x-ray diffraction analysis confirmed that properly processed films possessed the orthorhombic distortion of the perovskite structure at room temperature. In response to a 1 kHz, sinusoidal field of 300 kV/cm amplitude, we measured the following ferroelectric properties: (1) a remanent polarization of 4.5 ..mu..C/cm/sup 2/, (2) a spontaneous polarization of 8.3 ..mu..C/cm/sup 2/, and (3) a coercive field of 55 kV/cm.