A microstructural analysis of solder joints from the electronic assemblies of dismantled nuclear weapons
MC1814 Interconnection Boxes from dismantled B57 bombs, and MC2839 firing Sets from retired W70-1 warheads were obtained from the Pantex facility. Printed circuit boards were selected from these components for microstructural analysis of their solder joints. The analysis included a qualitative examination of the solder joints and quantitative assessments of (1) the thickness of the intermetallic compound layer that formed between the solder and circuit board Cu features, and (2) the Pb-rich phase particle distribution within the solder joint microstructure. The MC2839 solder joints had very good workmanship qualities. The intermetallic compound layer stoichiometry was determined to be that of Cu6Sn5. The mean intermetallic compound layer thickness for all solder joints was 0.885 mm. The magnitude of these values did not indicate significant growth over the weapon lifetime. The size distribution of the Pb-rich phase particles for each of the joints were represented by the mean of 9.85 {times} 10{sup {minus}6} mm{sup 2}. Assuming a spherical geometry, the mean particle diameter would be 3.54 mm. The joint-to-joint difference of intermetallic compound layer thickness and Pb-rich particle size distribution was not caused by varying thermal environments, but rather, was a result of natural variations in the joint microstructure that probably existed at the time of manufacture. The microstructural evaluation of the through-hole solder joints form the MC2839 and MC1814 components indicated that the environmental conditions to which these electronic units were exposed in the stockpile, were benign regarding solder joint aging. There was an absence of thermal fatigue damage in MC2839 circuit board, through-hole solder joints. The damage to the eyelet solder joints of the MC1814 more likely represented infant mortality failures at or very near the time of manufacture, resulting from a marginal design status of this type of solder joint design.