Publications

Abstract not provided.

In this work, scratch and nanoindentation testing was used to determine hardness, fracture toughness, strain rate sensitivity, and activation volumes on additively manufactured graded and uniform Ni-Nb bulk specimens. Characterization showed the presence of a two phase system consisting of Ni₃Nb and Ni₆Nb₇ intermetallics. Intermetallics were multimodal in nature, having grain and cell sizes spanning from a few nanometers to 10s of micrometers. The unique microstructure resulted in impressively high hardness, up to 20 GPa in the case of the compositionally graded sample. AM methods with surface deformation techniques are a useful way to rapidly probe material properties and alloy composition space.

In this work, scratch and nanoindentation testing was used to determine hardness, fracture toughness, strain rate sensitivity, and activation volumes on additively manufactured graded and uniform Ni-Nb bulk specimens. Characterization showed the presence of a two phase system consisting of Ni₃Nb and Ni₆Nb₇ intermetallics. Intermetallics were multimodal in nature, having grain and cell sizes spanning from a few nanometers to 10s of micrometers. The unique microstructure resulted in impressively high hardness, up to 20 GPa in the case of the compositionally graded sample. AM methods with surface deformation techniques are a useful way to rapidly probe material properties and alloy composition space.

Abstract not provided.

Abstract not provided.

Heterojunctions of semiconductors and metals are the fundamental building blocks of modern electronics. Coherent heterostructures between dissimilar materials can be achieved by composition, doping, or heteroepitaxy of chemically different elements. Here, we report the formation of coherent single-layer 1H-1T MoS2 heterostructures by mechanical exfoliation on Au(111), which are chemically homogeneous with matched lattices but show electronically distinct semiconducting (1H phase) and metallic (1T phase) character, with the formation of these heterojunctions attributed to a combination of lattice strain and charge transfer. The exfoliation approach employed is free of tape residues usually found in many exfoliation methods and yields single-layer MoS2 with millimeter (mm) size on the Au surface. Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), scanning tunneling microscopy (STM), and scanning tunneling spectroscopy (STS) have collectively been employed to elucidate the structural and electronic properties of MoS2 monolayers on Au substrates. Bubbles in the MoS2 formed by the trapping of ambient adsorbates beneath the single layer during deposition, have also been observed and characterized. Our work here provides a basis to produce two-dimensional heterostructures which represent potential candidates for future electronic devices.

We present evidence of inverse Hall-Petch behavior for a single-phase high entropy alloy (CoCrFeMnNi) in ultra-high vacuum and show that it is associated with low friction coefficients (~0.3). Grain size measurements by STEM validate a recently proposed dynamic amorphization model that accurately predicts grain size-dependent shear strength in the inverse Hall-Petch regime. Wear rates in the initially soft (coarse grained) material were shown to be remarkably low (~10–6 mm3/N-m), the lowest for any HEA tested in an inert environment where oxidation and the formation of mixed metal-oxide films is mitigated. The combined high wear resistance and low friction are linked to the formation of an ultra-nanocrystalline near-surface layer. The dynamic amorphization model was also used to predict an average high angle grain boundary energy (0.87 J/m2). This value was used to explain cavitation-induced nanoporosity found in the highly deformed surface layer, a phenomenon that has been linked to superplasticity.

Abstract not provided.

Refractory High Entropy Alloys (RHEAs) and Refractory Complex Concentrated Alloys (RCCAs) are high-temperature structural alloys ideally suited for use in harsh environments. While these alloys have shown promising structural properties at high temperatures that exceed the practical limits of conventional alloys, such as Ni-based superalloys, exploration of the complex phase-space of these materials remains a significant challenge. We report on a high-throughput alloy processing and characterization methodology, leveraging laser-based metal additive manufacturing (AM) and mechanical testing techniques, to enable rapid exploration of RHEAs/RCCAs. We utilized in situ alloying and compositional grading, unique to AM processing, to rapidly-produce RHEAs/RCCAs using readily available and inexpensive commercial elemental powders. We demonstrate this approach with the MoNbTaW alloy system, as a model material known for having exceptionally high strength at elevated temperature when processed using conventional methods (e.g., casting). Microstructure analysis, chemical composition, and strain rate dependent hardness of AM-processed material are presented and discussed in the context of understanding the structure-properties relationships of RHEAs/RCCAs.

Low friction is demonstrated with pure polycrystalline tantalum sliding contacts in both molecular dynamics simulations and ultrahigh vacuum experiments. This phenomenon is shown to be correlated with deformation occurring primarily through grain boundary sliding and can be explained using a recently developed predictive model for the shear strength of metals. Specifically, low friction is associated with grain sizes at the interface being smaller than a critical, material-dependent value, where a crossover from dislocation mediated plasticity to grain-boundary sliding occurs. Low friction is therefore associated with inverse Hall-Petch behavior and softening of the interface. Direct quantitative comparisons between experiments and atomistic calculations are used to illustrate the accuracy of the predictions.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Nanocrystalline metals offer significant improvements in structural performance over conventional alloys. However, their performance is limited by grain boundary instability and limited ductility. Solute segregation has been proposed as a stabilization mechanism, however the solute atoms can embrittle grain boundaries and further degrade the toughness. In the present study, we confirm the embrittling effect of solute segregation in Pt–Au alloys. However, more importantly, we show that inhomogeneous chemical segregation to the grain boundary can lead to a new toughening mechanism termed compositional crack arrest. Energy dissipation is facilitated by the formation of nanocrack networks formed when cracks arrested at regions of the grain boundaries that were starved in the embrittling element. This mechanism, in concert with triple junction crack arrest, provides pathways to optimize both thermal stability and energy dissipation. A combination of in situ tensile deformation experiments and molecular dynamics simulations elucidate both the embrittling and toughening processes that can occur as a function of solute content.

This SAND report fulfills the final report requirement for the Born Qualified Grand Challenge LDRD. Born Qualified was funded from FY16-FY18 with a total budget of ~$13M over the 3 years of funding. Overall 70+ staff, Post Docs, and students supported this project over its lifetime. The driver for Born Qualified was using Additive Manufacturing (AM) to change the qualification paradigm for low volume, high value, high consequence, complex parts that are common in high-risk industries such as ND, defense, energy, aerospace, and medical. AM offers the opportunity to transform design, manufacturing, and qualification with its unique capabilities. AM is a disruptive technology, allowing the capability to simultaneously create part and material while tightly controlling and monitoring the manufacturing process at the voxel level, with the inherent flexibility and agility in printing layer-by-layer. AM enables the possibility of measuring critical material and part parameters during manufacturing, thus changing the way we collect data, assess performance, and accept or qualify parts. It provides an opportunity to shift from the current iterative design-build-test qualification paradigm using traditional manufacturing processes to design-by-predictivity where requirements are addressed concurrently and rapidly. The new qualification paradigm driven by AM provides the opportunity to predict performance probabilistically, to optimally control the manufacturing process, and to implement accelerated cycles of learning. Exploiting these capabilities to realize a new uncertainty quantification-driven qualification that is rapid, flexible, and practical is the focus of this effort.

Abstract not provided.