Abstract not provided.

Selectively oxidized vertical cavity lasers emitting at 1294 nm using InGaAsN quantum wells are reported for the first time which operate continuous wave at and above room temperature. The lasers employ two n-type Al{sub 0.94}Ga{sub 0.06}As/GaAs distributed Bragg reflectors each with a selectively oxidized current aperture adjacent to the optical cavity, and the top output mirror contains a tunnel junction to inject holes into the active region. Continuous wave single mode lasing is observed up to 55 C. These lasers exhibit the longest wavelength reported to date for vertical cavity surface emitting lasers grown on GaAs substrates.

In-plane magnetic field photoluminescence spectra from n series of n-type modulation doped GaAs/Al{sub 0.3}Ga{sub 0.7}As coupled double quantum wells show distinctive doublet structures related to the tunnel-split ground sub-level states. The magnetic field behavior of the upper transition from the antisymmetric state strongly depends on sample mobility. In a lower mobility sample, the transition energy displays an N-type kink with field (namely a maximum followed by a minimum), whereas higher mobility samples have a linear dependence. The former is attributed to a coupling mechanism due to homogeneous broadening of the electron and hole states. The results are in good agreement with recent theoretical calculations.

The authors have investigated the properties of GaAsSb/InGaAs type-II bilayer quantum well structures grown by molecule beam epitaxy for use in long-wavelength lasers on GaAs substrates. Structures with layer, strains and thicknesses designed to be thermodynamically stable against dislocation formation exhibit room-temperature photoluminescence at wavelengths as long as 1.43 {mu}m. The photoluminescence emission wavelength is significantly affected by growth temperature and the sequence of layer growth (InGaAs/GaAsSb vs GaAsSb/InGaAs), suggesting that Sb and/or In segregation results in non-ideal interfaces under certain growth conditions. At low injection currents, double heterostructure lasers with GaAsSb/InGaAs bilayer quantum well active regions display electroluminescence at wavelengths comparable to those obtained in photoluminescence, but at higher currents the electroluminescence shifts to shorter wavelengths. Lasers have been obtained with threshold current densities as low as 120 A/cm{sup 2} at 1.17 {mu}m, and 2.1 kA/cm{sup 2} at 1.21 {mu}m.

Strained-layer semiconductor films offer tremendous potential with regards to optoelectronic applications for high speed communications, mobile communications, sensing, and novel logic devices. It is an unfortunate reality that many of the possible film/substrate combinations that could be exploited technologically are off limits because of large differences in lattice parameters, chemical compatibilities, or thermal expansion rates. These mechanical, chemical, and thermal incompatibilities manifest themselves primarily in terms of lattice defects such as dislocations and antiphase boundaries, and in some cases through enhanced surface roughness. An additional limitation, from a production point of view, is money. Device manufacturers as a rule want the cheapest substrate possible. Freeing the heteroepitaxial world of the bonds of (near) lattice matching would vastly expand the types of working devices that could be grown. As a result, a great deal of effort has been expended finding schemes to integrate dissimilar film/substrate materials while preserving the perfection of the film layer. One such scheme receiving significant attention lately is the so-called compliant substrate approach.

The authors report data on GaAsSb single quantum well lasers grown on GaAs substrates. Room temperature pulsed emission at 1.275 {micro}m in a 1,250 {micro}m-long device has been observed. Minimum threshold current densities of 535 A/cm{sup 2} were measured in 2000 {micro}m long lasers. The authors also measured internal losses of 2--5 cm{sup {minus}1}, internal quantum efficiencies of 30-38% and characteristic temperature T{sub 0} of 67--77 C. From these parameters a gain constant G{sub 0} of 1,660 cm{sup {minus}1} and a transparency current density J{sub tr} of 134 A/cm{sup 2} were calculated. The results indicate the potential for fabricating 1.3 {micro}m VCSELs from these materials.

A high voltage GaAs HBT with an open-base collector breakdown voltage of 106 V and an open-emitter breakdown voltage of 134 V has been demonstrated. A high quality 9.0 {micro}m thick collector doped to 2.0{times}10{sup 15} cm{sup {minus}3} grown by MBE on a doped GaAs substrate is the key to achieving this breakdown. These results were achieved for HBTs with 4{times}40 {micro}m{sup 2} emitters. DC current gain of 38 at 6,000 A/cm{sup 2} was measured.

This LDRD project explored the fundamental physics of a new class of photonic materials, photonic bandgap structures (PBG), and examine its unique properties for the design and implementation of photonic devices on a nano-meter length scale for the control and confinement of light. The low loss, highly reflective and quantum interference nature of a PBG material makes it one of the most promising candidates for realizing an extremely high-Q resonant cavity, >10,000, for optoelectronic applications and for the exploration of novel photonic physics, such as photonic localization, tunneling and modification of spontaneous emission rate. Moreover, the photonic bandgap concept affords us with a new opportunity to design and tailor photonic properties in very much the same way we manipulate, or bandgap engineer, electronic properties through modern epitaxy.

Abstract not provided.

Mixed arsenide/antimonide materials have unique properties which make them potentially valuable for use in VCSELs operating at wavelengths longer than 1 {micro}m. The authors present their progress in applying these materials to VCSEL designs for 1--1.55 {micro}m.

Short communication.