Publications

This report summarizes materials issues associated with advanced micromachines development at Sandia. The intent of this report is to provide a perspective on the scope of the issues and suggest future technical directions, with a focus on computational materials science. Materials issues in surface micromachining (SMM), Lithographic-Galvanoformung-Abformung (LIGA: lithography, electrodeposition, and molding), and meso-machining technologies were identified. Each individual issue was assessed in four categories: degree of basic understanding; amount of existing experimental data capability of existing models; and, based on the perspective of component developers, the importance of the issue to be resolved. Three broad requirements for micromachines emerged from this process. They are: (1) tribological behavior, including stiction, friction, wear, and the use of surface treatments to control these, (2) mechanical behavior at microscale, including elasticity, plasticity, and the effect of microstructural features on mechanical strength, and (3) degradation of tribological and mechanical properties in normal (including aging), abnormal and hostile environments. Resolving all the identified critical issues requires a significant cooperative and complementary effort between computational and experimental programs. The breadth of this work is greater than any single program is likely to support. This report should serve as a guide to plan micromachines development at Sandia.

Direct metal deposition technologies produce complex, near net shape components from Computer Aided Design (CAD) solid models. Most of these techniques fabricate a component by melting powder in a laser weld pool, rastering the weld bead to form a layer, and additively constructing subsequent layers. This report will describe anew direct metal deposition process, known as WireFeed, whereby a small diameter wire is used instead of powder as the feed material to fabricate components. Currently, parts are being fabricated from stainless steel alloys. Microscopy studies show the WireFeed parts to be filly dense with fine microstructural features. Mechanical tests show stainless steel parts to have high strength values with retained ductility. A model was developed to simulate the microstructural evolution and coarsening during the WireFeed process. Simulations demonstrate the importance of knowing the temperature distribution during fabrication of a WireFeed part. The temperature distribution influences microstructural evolution and, therefore, must be controlled to tailor the microstructure for optimal performance.