Exploding bridgewire detonators (EBWs) containing pentaerythritol tetranitrate (PETN) exposed to high temperatures may not function following discharge of the design electrical firing signal from a charged capacitor. Knowing functionality of these arbitrarily facing EBWs is crucial when making safety assessments of detonators in accidental fires. Orientation effects are only significant when the PETN is partially melted. The melting temperature can be measured with a differential scanning calorimeter. Nonmelting EBWs will be fully functional provided the detonator never exceeds 406 K (133 °C) for at least 1 h. Conversely, EBWs will not be functional once the average input pellet temperature exceeds 414 K (141 °C) for a least 1 min which is long enough to cause the PETN input pellet to completely melt. Functionality of the EBWs at temperatures between 406 and 414 K will depend on orientation and can be predicted using a stratification model for downward facing detonators but is more complex for arbitrary orientations. A conservative rule of thumb would be to assume that the EBWs are fully functional unless the PETN input pellet has completely melted.
Exploding bridgewire (EBW) detonators are used to rapidly and reliably initiate energetic reactions by exploding a bridgewire via Joule heating. While the mechanisms of EBW detonators have been studied extensively in nominal conditions, comparatively few studies have addressed thermally damaged detonator operability. We present a mesoscale simulation study of thermal damage in a representative EBW detonator, using discrete element method (DEM) simulations that explicitly account for individual particles in the pressed explosive powder. We use a simplified model of melting, where solid spherical particles undergo uniform shrinking, and fluid dynamics are ignored. The subsequent settling of particles results in the formation of a gap between the solid powder and the bridgewire, which we study under different conditions. In particular, particle cohesion has a significant effect on gap formation and settling behavior, where sufficiently high cohesion leads to coalescence of particles into a free-standing pellet. This behavior is qualitatively compared to experimental visualization data, and simulations are shown to capture several key changes in pellet shape. We derive a minimum and maximum limit on gap formation during melting using simple geometric arguments. In the absence of cohesion, results agree with the maximum gap size. With increasing cohesion, the gap size decreases, eventually saturating at the minimum limit. We present results for different combinations of interparticle cohesion and detonator orientations with respect to gravity, demonstrating the complex behavior of these systems and the potential for DEM simulations to capture a range of scenarios.
Determining the thermal response of energetic materials at high densities can be difficult when pressure dependent reactions occur within the interior of the material. At high temperatures, reactive components such as hexahydro-l,3,5-tri-nitro-l,3,5-triazine (RDX), ammonium perchlorate (AP), and hydroxyl-terminated polybutadiene (HTPB) decompose and interact. The decomposition products accumulate near defects where internal pressure ultimately causes mechanical damage with closed pores transitioning into open pores. Gases are no longer confined locally; instead, they freely migrate between open pores and ultimately escape into the surrounding headspace or vent. Recently we have developed a universal cookoff model (UCM) coupled to a micromechanics pressurization (MMP) model to address pressure-dependent reactions that occur within the interior of explosives. Parameters for the UCM/MMP model are presented for an explosive and two propellants that contain similar portions of both aluminum (Al) and a binder. The explosive contains RDX and the propellants contain AP with no RDX. One of the propellants contains small amounts of curing catalysts and a burn modifier whereas the other propellant does not. We found that the cookoff behavior of the two propellants behave similarly leading and conclude that small amounts of catalysts or burn modifiers do not influence cookoff behavior appreciably. Kinetic parameters for the UCM/MMP models were obtained from the Sandia Instrumented Thermal Ignition (SITI) experiment. Validation is done with data from other laboratories.
Exploding bridgewire detonators (EBWs) containing pentaerythritol tetranitrate (PETN) exposed to high temperatures may not function following discharge of the design electrical firing signal from a charged capacitor. Knowing functionality of these arbitrarily facing EBWs is crucial when making safety assessments of detonators in accidental fires. Orientation effects are only significant when the PETN is partially melted. Here, the melting temperature can be measured with a differential scanning calorimeter. Nonmelting EBWs will be fully functional provided the detonator never exceeds 406 K (133 °C) for at least 1 h. Conversely, EBWs will not be functional once the average input pellet temperature exceeds 414 K (141 °C) for a least 1 min which is long enough to cause the PETN input pellet to completely melt. Functionality of the EBWs at temperatures between 406 and 414 K will depend on orientation and can be predicted using a stratification model for downward facing detonators but is more complex for arbitrary orientations. A conservative rule of thumb would be to assume that the EBWs are fully functional unless the PETN input pellet has completely melted.
Large rocket motors may violently explode when exposed to accidental fires. Even hot metal fragments from a nearby accident may penetrate the propellant and ultimately cause thermal ignition. A mechanistic understanding of heated propellants leading to thermal runaway is a major unsolved problem. Here we show that thermal ignition in propellants can be predicted using a universal cookoff model coupled to a micromechanics pressurization model. Our model predicts the time to thermal ignition in cookoff experiments with variable headspace volumes. We found that experiments with headspace volumes are more prone to deformation which distorts pores and causes increased permeability when the propellant expands into this headspace. Delayed ignition with larger headspace volume correlates with lower headspace pressures during decomposition. We found that our predictions matched experimental measurements best when the initial propellant was impermeable to gas flow rather than being permeable. Similar behavior is expected with other energetic materials with rubbery binders. Our model is validated using data from a separate laboratory. We also present an uncertainty analysis using Latin Hypercube Sampling (LHS) of thermal ignition caused by a steel fragment embedded in the propellant.
Understanding titanium particle combustion processes is critical not only for characterizing existing pyrotechnic systems but also for creating new igniter designs. In order to characterize titanium particle combustion processes, morphologies, and temperatures, simultaneous spatially-resolved electric field holography and imaging pyrometry techniques were used to capture post-ignition data at up to 7 kHz. Due to the phase and thermal distortions present in the combustion cloud, traditional digital in-line holography techniques fail to capture accurate data. In this work, electric field holography techniques are used in order to cancel distortions and capture the three-dimensional spatial locations and diameters of the particles. In order to estimate the projected surface temperatures of the titanium particles, an imaging pyrometry method that ratios emission at 750 and 850 nm is utilized. Using these diagnostics, joint statistics are collected for particle size, morphology, velocity, and temperature. Results show that, early in the combustion process, the titanium particles are primarily oxidized by potassium perchlorate inside the igniter cup, resulting in projected surface temperatures near 3000 K. Later in the process, the particles interact with ambient air, resulting in lower surface temperatures around 2400 K and the formation of flame zones. These results are consistent with adiabatic flame temperature predictions as well as particle morphology observations of a titanium core with a TiO2 surface. Late stage particle expansion, star fragmentation, and molten droplet breakup events are also observed using the time-resolved morphology and temperature diagnostics. These results illustrate the different stages of titanium particle combustion in pyrotechnic environments, which can be used to inform improvements in next-generation igniters.
Hobbs, Michael L.; Britt, Phillip F.; Hobbs, David T.; Kaneshige, Michael; Minette, Michael; Mintz, Jessica; Pennebaker, Frank M.; Parker, Gary R.; Rosenberg, David; Schwantes, Jon; Williams, Audrey; Pierce, Robert
Hobbs, Michael L.; Britt, Phillip F.; Hobbs, David T.; Kaneshige, Michael; Minette, Michael; Mintz, Jessica; Pennebaker, Frank M.; Parker, Gary R.; Pierce, Robert; Rosenberg, David; Schwantes, Jon; Williams, Audrey
Precise wording is important in every field of study, including operational procedures. Confusion in the wording “organic” and “inorganic” may have contributed to substitution of an organic kitty litter for an inorganic adsorbent used to prepare nuclear waste for disposal at an underground salt repository. Adsorbents prevent liquids like nitric acid from causing corrosion within the waste drums. However, combination of organic material with nitric acid can cause heat- and gas-generating reactions resulting in thermal runaway, rapid pressurization, and drum rupture. In 2014, waste Drum 68660 containing nitric acid-soaked organic kitty litter exploded and released transuranic waste into the repository. The cause of the accident was never identified. Here we show that the root cause of Drum 68660 igniting was restriction of the drum vent resulting in accelerated nitric acid chemistry, thermal runaway, and radiation dispersal.
In previous work, commercially available downward facing exploding bridgewire detonators (EBWs) were exposed to elevated temperatures. These detonators were then initiated using a firing set which discharged a high amplitude short duration electrical pulse into a thin gold bridgewire. Responses of the detonators were measured using photonic doppler velocimetry (PDV) and high-speed photography. A time delay of 2 μs between EBW initiation and first movement of an output flyer separated operable detonators from inoperable detonators or duds. In the current work, we propose a simple method to determine detonator operability from the calculated state of the detonator at the time the firing set is initiated. The failure criterion is based on the gap distance between the exploding bridgewire (EBW) and the adjacent initiating explosive within the detonator which is low-density pentaerythritol tetranitrate (PETN) that melts between 413–415 K (140–142 °C). The gap forms as PETN melts and flows to the bottom of the input pellet. Melting of PETN is modeled thermodynamically as an energy sink using a normal distribution spread over a temperature range between the onset temperature of 413 K and the ending temperature of 415 K. The extent of the melt is determined from the average temperature of the PETN. The PETN liquid is assumed to occupy the interstitial gas volume in the lower part of the input pellet. The vacated volume from the relocated liquid forms the gap between the EBW and the PETN. The remaining sandwiched layer consists of solid PETN particles and gas filling interstitial volume. We predict that a threshold gap between 17–27 μm separates properly functioning detonators from duds.
Operability thresholds that differentiate between functional RP-87 exploding bridge wire (EBW) detonators and nonfunctional RP-87 EBW detonators (duds) were determined by measuring the time delay between initiation and early wall movement (function time). The detonators were inserted into an externally heated hollow cylinder of aluminum and fired with current flow from a charged capacitor using an exploding bridge wire (EBW initiated). Functioning detonators responded like unheated pristine detonators when the function time was 4 μs or less. The operability thresholds of the detonators were characterized with a simple decomposition cookoff model calibrated using a modified version of the Sandia Instrumented Thermal Ignition (SITI) experiment. These thresholds are based on the calculated state of the PETN when the detonators fire. The operability threshold is proportional to the positive temperature difference (ΔT) between the maximum temperature within the PETN and the onset of decomposition (∼406 K). The temperature difference alone was not sufficient to define the operability threshold. The operability threshold was also proportional to the time that the PETN had been at elevated temperatures. That is, failure was proportional to both temperature and reaction rate. The reacted gas fraction is used in the current work for the reaction correlation. Melting of PETN also had a significant effect on the operability threshold. Detonator failure occurred when the maximum temperature exceeded the nominal melting point of PETN (414 K) for 45±5 s or more.
This is the Sandia report from a joint NSRD project between Sandia National Labs and Savannah River National Labs. The project involved development of simulation tools and data intended to be useful for tritium operations safety assessment. Tritium is a synthetic isotope of hydrogen that has a limited lifetime, and it is found at many tritium facilities in the form of elemental gas (T2). The most serious risk of reasonable probability in an accident scenario is when the tritium is released and reacts with oxygen to form a water molecule, which is subsequently absorbed into the human body. This tritium oxide is more readily absorbed by the body and therefore represents a limiting factor for safety analysis. The abnormal condition of a fire may result in conversion of the safer T2 inventory to the more hazardous oxidized form. It is this risk that tends to govern the safety protocols. Tritium fire datasets do not exist, so prescriptive safety guidance is largely conservative and reliant on means other than testing to formulate guidelines. This can have a consequence in terms of expensive and/or unnecessary mitigation design, handling protocols, and operational activities. This issue can be addressed through added studies on the behavior of tritium under representative conditions. Due to the hazards associated with the tests, this is being approached mainly from a modeling and simulation standpoint and surrogate testing. This study largely establishes the capability to generate simulation predictions with sufficiently credible characteristics to be accepted for safety guidelines as a surrogate for actual data through a variety of testing and modeling activities.
Transforming polymorphs, melting, and boiling are physical processes that can accelerate decomposition rates during cookoff of PETN and make measurements difficult. For example, splashing liquids from large bubbles filled with decomposition products clog pressure tubing in sealed experiments. Boil over can also extinguish thermal excursions in vented experiments making ignition difficult. For better measurements, we have modified the Sandia Instrumented Thermal Ignition (SITI) experiment to obtain better sealed and vented cookoff data for PETN by reducing the sample size and including additional gas space to prevent clogged tubing and boil over. Ignition times were not affected by 1) increasing the gas space by a factor of 3 in sealed SITI experiments or by 2) venting the decomposition gasses. That is, thermal ignition of PETN is not pressure dependent and the rate-limiting step during PETN decomposition likely occurs in the condensed phase. A simple decomposition model was calibrated using these observations and includes rate acceleration caused by melting and boiling. The model is used to predict internal temperatures, pressurization, and thermal ignition in a wide variety of experiments. The model is also used with SITI data to estimate the previously unreported latent enthalpy (5 J/g) associated with the α (PETN-I) to β (PETN-II) polymorphic phase transformation of PETN.
Cookoff experiments of powdered and pressed TATB-based plastic bonded explosives (PBXs) have been modeled using a pressure-dependent universal cookoff model (UCM) in combination with a micromechanics pressurization (MMP) model described in a companion paper. The MMP model is based on the accumulation of decomposition gases at nucleation sites that load the surrounding TATB crystals and binder. This is the first cookoff model to use an analytical mechanics solution for compressibility and thermal expansion to describe internal pressurization caused by both temperature and decomposition occurring within closed-pore explosives. This approach produces more accurate predictions of ignition time and pressurization within high-density explosives than simple equation-of-state models. The current paper gives details of the reaction chemistry, model parameters, predicted uncertainty, and validation using experiments from multiple laboratories with errors less than 6 %. The UCM/MMP model framework gives more accurate thermal ignition predictions for high density explosives that are initially impermeable to decomposition gases.