The effects of dose, dose rate, and irradiation type and their equivalence on radiation-induced segregation in binary alloy systems via phase-field simulations

Vizoso, Daniel; Deo, Deo; Dingreville, Remi P.

Radiation-induced segregation is a phenomenon commonly observed in many alloys which consists of the redistribution of elements (solute or interstitial impurities) under irradiation. The onset and development of radiation-induced segregation can only occur when a sufficient flux of defects is sustained and defect sinks are present. Irradiation dose, dose rate, and particle types all affect defect flux. In this work, we employ a phase-field model to examine the effects of dose, dose rate, and type of incident particles on radiation-induced segregation behavior in a model binary alloy. The phase-field model takes into account the formation and evolution of point defects as well as defect clusters, the diffusion and clustering of alloy species, the presence of additional extrinsic defect sinks in the form of dislocations, and two different methods of radiation-damage insertion, which are intended to simulate either light-ion/electron irradiation via Frenkel pairs or heavy-ion irradiation in the form of cascades. Our results show a dose-rate and particle-type dependence on the amount of solute segregation. We show that the material systems exposed to higher dose rates are less subjected to solute segregation at equivalent doses. We also show that such dose-rate-dependence behavior is due to a delay of the incubation dose at which radiation-induced segregation effectively starts. Particle type and the presence of dislocations can accentuate this behavior. Our model predictions correlate with many experimental observations made over the years on radiation-induced segregation providing credence to the simulation results. The methodology presented in this study allows for a first-order prediction of the dose rate at which proxy irradiation experiments could be performed to approximate radiation-induced segregation behaviors seen in targeted irradiation conditions.