(Harvard University) Neutron diffraction was employed to measure internal residual stresses at various locations along stainless steel (SS) 17-4 PH specimens additively manufactured via laser-powder bed fusion (L-PBF). Of these specimens, two were rods (diameter = 8 mm, length = 80 mm) built vertically upward and one a parallelepiped (8 × 80 x 9 mm3) built with its longest edge parallel to ground. One rod and the parallelepiped were left in their as-built condition, while the other rod was heat treated. Data presented provide insight into the microstructural characteristics of typical L-PBF SS 17-4 PH specimens and their dependence on build orientation and post-processing procedures such as heat treatment.
Link to Dataset
Residual Stress Measurements via Neutron Diffraction of Additive Manufactured Stainless Steel 17-4 PH
Date last updated: April 23, 2017