Skip to main content
  • Thermosets
    • 828/DEA
      • 828/DEA: Shear Modulus vs Temp
      • 828/DEA: Master Curve
      • 828/DEA: Linear CTE vs Temp
      • 828/DEA: Bulk Modulus vs Temp
      • 828/DEA: Heat Capacity vs Temp
      • 828/DEA: Compressive Yield
      • 828/DEA: Tensile Yield
      • 828/DEA: Tensile Creep for Fast Cooling Rate
      • 828/DEA: Tensile Creep for Slow Cooling Rate
      • 828/DEA: Cohesive Failure
      • 828/DEA: Adhesive Failure
      • 828/DEA: Pre-Reaction Kinetics
      • 828/DEA: Gelation Reaction Kinetics
      • 828/DEA: Viscosity Increase During Cure
      • 828/DEA: Cure Shrinkage
      • 828/DEA: Tg During Cure
      • 828/DEA: Cohesive Strength During Cure
    • 828/DEA/GMB
      • 828/DEA/GMB: Shear Modulus vs Temp
      • 828/DEA/GMB: Master Curve
      • 828/DEA/GMB: Linear CTE vs Temp
      • 828/DEA/GMB: K, Density, and Failure
      • 828/DEA/GMB: Heat Capacity vs Temp
      • 828/DEA/GMB: Compressive Yield
      • 828/DEA/GMB: Gelation Reaction Kinetics
      • 828/DEA/GMB: Viscosity Increase During Cure
    • 826/CTBN/DEA
      • 826/CTBN/DEA: Shear Modulus vs Temp
      • 826/CTBN/DEA: Master Curve
      • 826/CTBN/DEA: Linear CTE vs Temp
      • 826/CTBN/DEA: Bulk Modulus and Density
      • 826/CTBN/DEA: Heat Capacity vs Temp
      • 826/CTBN/DEA: Compressive Yield
    • 828/CTBN/DEA/GMB
      • 828/CTBN/DEA/GMB: Shear Modulus vs Temp
      • 828/CTBN/DEA/GMB: Master Curve
      • 828/CTBN/DEA/GMB: Linear CTE vs Temp
      • 828/CTBN/DEA/GMB: K, Density, and Failure
      • 828/CTBN/DEA/GMB: Heat Capacity vs Temp
      • 828/CTBN/DEA/GMB: Compressive Yield
      • 828/CTBN/DEA/GMB: Viscosity Increase During Cure
    • 828/DEA/Silica
      • 828/DEA/Silica: Shear Modulus vs Temp
      • 828/DEA/Silica: Master Curve
      • 828/DEA/Silica: Linear CTE vs Temp
      • 828/DEA/Silica: Heat Capacity vs Temp
      • 828/DEA/Silica: Bulk Modulus and Density
      • 828/DEA/Silica (45vol%): Compressive Yield
      • 828/DEA/Silica (30vol%): Compressive Yield
    • 828/Z
      • 828/Z: Shear Modulus vs Temp
      • 828/Z: Linear CTE vs Temp
      • 828/Z: Bulk Modulus and Cohesive Failure
      • 828/Z: Heat Capacity vs Temp
      • 828/Z: Compressive Yield
      • 828/Z: Gelation Reaction Kinetics
      • 828/Z: Viscosity Increase During Cure
      • 828/Z: Tg During Cure
    • 828/Z/Alox
      • 828/Z/Alox: Shear Modulus vs Temp
      • 828/Z/Alox: Linear CTE vs Temp
      • 828/Z/Alox: Bulk Modulus and Cohesive Failure
      • 828/Z/Alox: Heat Capacity vs Temp
      • 828/Z/Alox: Compressive Yield
    • 828/Z/Mica
      • 828/Z/Mica: Shear Modulus vs Temp
      • 828/Z/Mica: Linear CTE vs Temp
      • 828/Z/Mica: Bulk Modulus and Cohesive Failure
      • 828/Z/Mica: Heat Capacity vs Temp
      • 828/Z/Mica: Compressive Yield
    • ANH2
      • ANH2: Linear CTE vs Temp
      • ANH2: Gelation Reaction Kinetics
    • 459
      • 459: Master Curve
      • 459: Linear CTE vs Temp
      • 459: Bulk Modulus and Failure
      • 459: Heat Capacity vs Temp
      • 459: Compressive Yield
      • 459: Gelation Reaction Kinetics
      • 459: Tg During Cure
    • 459/GMB
      • 459/GMB: Shear Modulus vs Temp
      • 459/GMB: Master Curve
      • 459/GMB: Linear CTE vs Temp
      • 459/GMB: Bulk Modulus and Failure
      • 459/GMB: Heat Capacity vs Temp
      • 459/GMB: Compressive Yield
    • 459/Alox
      • 459/Alox: Shear Modulus vs Temp
      • 459/Alox: Master Curve
      • 459/Alox: Linear CTE vs Temp
      • 459/Alox: Bulk Modulus and Failure
      • 459/Alox: Heat Capacity vs Temp
      • 459/Alox: Compressive Yield
    • 828/D230
      • 828/D230: Shear Modulus vs Temp
      • 828/D230: Master Curve
      • 828/D230: Linear CTE vs Temp
      • 828/D230: Yield
      • 828/D230: Tensile Creep at 23C
      • 828/D230: Gelation Reaction Kinetics
      • 828/D230: Viscosity Increase During Cure
      • 828/D230: Shear Modulus During Cure
      • 828/D230: Tg During Cure
      • 828/D230: Cure Shrinkage
      • Curative: Weight Loss
    • 828/D230/GMB
      • 828/D230/GMB: Shear Modulus vs Temp
      • 828/D230/GMB: Linear CTE vs Temp
      • 828/D230/GMB: Bulk Modulus and Density
      • 828/D230/GMB: Viscosity Increase During Cure
    • 828/D230/Alox
      • 828/D230/A20SG: Shear Modulus vs Temp
      • 828/D230/A20SG: Linear CTE vs Temp
      • 828/D230/A20SG: Bulk Modulus and Density
      • 828/D230/A20SG(20vol%): Compressive Yield
      • 828/D230/A20SG(30vol%): Compressive Yield
      • 828/D230/A20SG(40vol%): Compressive Yield
    • 828/T403
      • 828/T403: Effect of 815C vs. 828
      • 828/T403: Gelation Reaction Kinetics
      • 828/T403: Viscosity Increase During Cure
    • 828/2049
      • 828/2049: Tg
      • 828/2049: Gelation Reaction Kinetics
  • Elastomers
    • Sylgard 184
      • Sylgard 184: Shear Modulus vs Temp
      • Sylgard with Silica: Linear CTE vs. vol% Filler
      • Sylgard 184: Young’s Modulus at 23C
      • Sylgard 184: Bulk Modulus at 22C
      • Sylgard 184: Adhesion Tests at 23C
      • Sylgard 184: Gelation Reaction Kinetics
      • Sylgard 184: Kinetics with 5% 3-6559 Accelerator
      • Sylgard 184: Viscosity with 5% 3-6559 Accelerator
      • Sylgard 184: Viscosity Increase During Cure
      • Sylgard 184: Viscosity with 5% 3-6559 Accelerator
    • Sylgard 184 / A16 GMB
      • Sylgard/A16: Shear Modulus vs Temp
      • Sylgard/A16: Linear CTE vs Temp
      • Sylgard/A16: Young’s Modulus at 23C
      • Sylgard/A16: Bulk Modulus at 23C
      • Sylgard/A16: Adhesion Tests at 23C
    • Sylgard 184 with Silica
      • Sylgard with Silica: Shear Modulus vs. vol% Filler
      • Sylgard with Silica: Linear CTE vs. vol% Filler
      • Sylgard with Silica: Density vs. vol% filler
    • CS3100 Polysulfide
      • CS3100: Shear Modulus vs Temp
      • CS3100: Linear CTE vs Temp
      • CS3100: Young’s Modulus at 23C
      • CS3100: Bulk Modulus at 23C
      • CS3100: Adhesion Tests at 23C
      • CS3100: Thermal Degradation
    • CS3100 Polysulfide with Phenolic Microballoons
      • CS3100/PMB: Shear Modulus vs Temp
      • CS3100/PMB: Linear CTE vs Temp
      • CS3100/PMB: Young’s Modulus at 23C
      • CS3100/PMB: Bulk Modulus at 23C
      • CS3100/PMB: Adhesion Tests at 23C
    • Arathane 5750 (previously Uralane)
      • 5750: Tensile Modulus vs Temp
      • 5750: Linear CTE vs Temp
    • Arathane 5753 (previously Uralane)
      • 5753: Tensile Modulus vs Temp
      • 5753: Linear CTE vs Temp
      • 5753: Viscosity Increase During Cure
    • EN11
      • EN11: Viscosity Increase During Cure
      • EN11: Tensile Modulus vs Temp
      • EN11: Linear CTE vs Temp
  • Misc
    • Polycarbonate
      • Polycarbonate: Master Curve
      • Polycarbonate: Linear CTE vs Temp
      • Polycarbonate: Compressive Yield
    • Mylar
      • Mylar: % Crystallinity
      • Mylar: Thermal Degradation
      • Mylar: Linear Strain vs Temp
      • Mylar: Tensile Modulus vs Temp
    • Nylon
      • Nylon: Master Curve
      • Nylon: Strain vs Temp
      • Nylon: Tensile Yield at 0C
    • Rexolite
      • Rexolite: Shear Modulus vs Temp
      • Rexolite: Linear CTE vs Temp
      • Rexolite: Compressive Yield at 23C
    • FR408 Composite
      • FR408: Stiffness Matrix at 23C
      • FR408: Linear CTEs vs Temp
  • Foams
    • 4 lb/ft3 PMDI
      • PMDI-4: Shear Modulus vs Temp
      • PMDI-4: Linear CTE vs Temp
      • PMDI-4: Compressive Yield at 23C
    • 6 lb/ft3 PMDI
      • PMDI-6: Shear Modulus vs Temp
      • PMDI-6: Linear CTE vs Temp
      • PMDI-6: Compressive Yield at 23C
    • 20 lb/ft3 PMDI
      • PMDI-20: Shear Modulus vs Temp
      • PMDI-20: Linear CTE vs Temp
      • PMDI-20: Effect of Postcure
      • PMDI-20: Compressive Yield at 23C
    • 10 lb/ft3 PMDI
      • PMDI-10: Shear Modulus vs Temp
      • PMDI-10: Compressive Yield at 23C
    • 6 lb/ft3 TufFoam
      • TufFoam-6: Shear Modulus vs Temp
      • TufFoam-6: Linear CTE vs temp
      • TufFoam-6: Compressive Yield at 23C
    • 10 lb/ft3 TufFoam
      • TufFoam-10: Shear Modulus vs Temp
      • TufFoam-10: Linear CTE vs Temp
      • TufFoam-10: Compressive Yield at 23C
    • 14 lb/ft3 TufFoam
      • TufFoam-14: Shear Modulus vs Temp
      • TufFoam-14: Linear CTE vs Temp
      • TufFoam-14: Compressive Yield at 23C
  • Thermosets
    • 828/DEA
      • 828/DEA: Shear Modulus vs Temp
      • 828/DEA: Master Curve
      • 828/DEA: Linear CTE vs Temp
      • 828/DEA: Bulk Modulus vs Temp
      • 828/DEA: Heat Capacity vs Temp
      • 828/DEA: Compressive Yield
      • 828/DEA: Tensile Yield
      • 828/DEA: Tensile Creep for Fast Cooling Rate
      • 828/DEA: Tensile Creep for Slow Cooling Rate
      • 828/DEA: Cohesive Failure
      • 828/DEA: Adhesive Failure
      • 828/DEA: Pre-Reaction Kinetics
      • 828/DEA: Gelation Reaction Kinetics
      • 828/DEA: Viscosity Increase During Cure
      • 828/DEA: Cure Shrinkage
      • 828/DEA: Tg During Cure
      • 828/DEA: Cohesive Strength During Cure
    • 828/DEA/GMB
      • 828/DEA/GMB: Shear Modulus vs Temp
      • 828/DEA/GMB: Master Curve
      • 828/DEA/GMB: Linear CTE vs Temp
      • 828/DEA/GMB: K, Density, and Failure
      • 828/DEA/GMB: Heat Capacity vs Temp
      • 828/DEA/GMB: Compressive Yield
      • 828/DEA/GMB: Gelation Reaction Kinetics
      • 828/DEA/GMB: Viscosity Increase During Cure
    • 826/CTBN/DEA
      • 826/CTBN/DEA: Shear Modulus vs Temp
      • 826/CTBN/DEA: Master Curve
      • 826/CTBN/DEA: Linear CTE vs Temp
      • 826/CTBN/DEA: Bulk Modulus and Density
      • 826/CTBN/DEA: Heat Capacity vs Temp
      • 826/CTBN/DEA: Compressive Yield
    • 828/CTBN/DEA/GMB
      • 828/CTBN/DEA/GMB: Shear Modulus vs Temp
      • 828/CTBN/DEA/GMB: Master Curve
      • 828/CTBN/DEA/GMB: Linear CTE vs Temp
      • 828/CTBN/DEA/GMB: K, Density, and Failure
      • 828/CTBN/DEA/GMB: Heat Capacity vs Temp
      • 828/CTBN/DEA/GMB: Compressive Yield
      • 828/CTBN/DEA/GMB: Viscosity Increase During Cure
    • 828/DEA/Silica
      • 828/DEA/Silica: Shear Modulus vs Temp
      • 828/DEA/Silica: Master Curve
      • 828/DEA/Silica: Linear CTE vs Temp
      • 828/DEA/Silica: Heat Capacity vs Temp
      • 828/DEA/Silica: Bulk Modulus and Density
      • 828/DEA/Silica (45vol%): Compressive Yield
      • 828/DEA/Silica (30vol%): Compressive Yield
    • 828/Z
      • 828/Z: Shear Modulus vs Temp
      • 828/Z: Linear CTE vs Temp
      • 828/Z: Bulk Modulus and Cohesive Failure
      • 828/Z: Heat Capacity vs Temp
      • 828/Z: Compressive Yield
      • 828/Z: Gelation Reaction Kinetics
      • 828/Z: Viscosity Increase During Cure
      • 828/Z: Tg During Cure
    • 828/Z/Alox
      • 828/Z/Alox: Shear Modulus vs Temp
      • 828/Z/Alox: Linear CTE vs Temp
      • 828/Z/Alox: Bulk Modulus and Cohesive Failure
      • 828/Z/Alox: Heat Capacity vs Temp
      • 828/Z/Alox: Compressive Yield
    • 828/Z/Mica
      • 828/Z/Mica: Shear Modulus vs Temp
      • 828/Z/Mica: Linear CTE vs Temp
      • 828/Z/Mica: Bulk Modulus and Cohesive Failure
      • 828/Z/Mica: Heat Capacity vs Temp
      • 828/Z/Mica: Compressive Yield
    • ANH2
      • ANH2: Linear CTE vs Temp
      • ANH2: Gelation Reaction Kinetics
    • 459
      • 459: Master Curve
      • 459: Linear CTE vs Temp
      • 459: Bulk Modulus and Failure
      • 459: Heat Capacity vs Temp
      • 459: Compressive Yield
      • 459: Gelation Reaction Kinetics
      • 459: Tg During Cure
    • 459/GMB
      • 459/GMB: Shear Modulus vs Temp
      • 459/GMB: Master Curve
      • 459/GMB: Linear CTE vs Temp
      • 459/GMB: Bulk Modulus and Failure
      • 459/GMB: Heat Capacity vs Temp
      • 459/GMB: Compressive Yield
    • 459/Alox
      • 459/Alox: Shear Modulus vs Temp
      • 459/Alox: Master Curve
      • 459/Alox: Linear CTE vs Temp
      • 459/Alox: Bulk Modulus and Failure
      • 459/Alox: Heat Capacity vs Temp
      • 459/Alox: Compressive Yield
    • 828/D230
      • 828/D230: Shear Modulus vs Temp
      • 828/D230: Master Curve
      • 828/D230: Linear CTE vs Temp
      • 828/D230: Yield
      • 828/D230: Tensile Creep at 23C
      • 828/D230: Gelation Reaction Kinetics
      • 828/D230: Viscosity Increase During Cure
      • 828/D230: Shear Modulus During Cure
      • 828/D230: Tg During Cure
      • 828/D230: Cure Shrinkage
      • Curative: Weight Loss
    • 828/D230/GMB
      • 828/D230/GMB: Shear Modulus vs Temp
      • 828/D230/GMB: Linear CTE vs Temp
      • 828/D230/GMB: Bulk Modulus and Density
      • 828/D230/GMB: Viscosity Increase During Cure
    • 828/D230/Alox
      • 828/D230/A20SG: Shear Modulus vs Temp
      • 828/D230/A20SG: Linear CTE vs Temp
      • 828/D230/A20SG: Bulk Modulus and Density
      • 828/D230/A20SG(20vol%): Compressive Yield
      • 828/D230/A20SG(30vol%): Compressive Yield
      • 828/D230/A20SG(40vol%): Compressive Yield
    • 828/T403
      • 828/T403: Effect of 815C vs. 828
      • 828/T403: Gelation Reaction Kinetics
      • 828/T403: Viscosity Increase During Cure
    • 828/2049
      • 828/2049: Tg
      • 828/2049: Gelation Reaction Kinetics
    • Sylgard 184
      • Sylgard 184: Shear Modulus vs Temp
      • Sylgard with Silica: Linear CTE vs. vol% Filler
      • Sylgard 184: Young’s Modulus at 23C
      • Sylgard 184: Bulk Modulus at 22C
      • Sylgard 184: Adhesion Tests at 23C
      • Sylgard 184: Gelation Reaction Kinetics
      • Sylgard 184: Kinetics with 5% 3-6559 Accelerator
      • Sylgard 184: Viscosity with 5% 3-6559 Accelerator
      • Sylgard 184: Viscosity Increase During Cure
      • Sylgard 184: Viscosity with 5% 3-6559 Accelerator
    • Sylgard 184 / A16 GMB
      • Sylgard/A16: Shear Modulus vs Temp
      • Sylgard/A16: Linear CTE vs Temp
      • Sylgard/A16: Young’s Modulus at 23C
      • Sylgard/A16: Bulk Modulus at 23C
      • Sylgard/A16: Adhesion Tests at 23C
    • Sylgard 184 with Silica
      • Sylgard with Silica: Shear Modulus vs. vol% Filler
      • Sylgard with Silica: Linear CTE vs. vol% Filler
      • Sylgard with Silica: Density vs. vol% filler
    • CS3100 Polysulfide
      • CS3100: Shear Modulus vs Temp
      • CS3100: Linear CTE vs Temp
      • CS3100: Young’s Modulus at 23C
      • CS3100: Bulk Modulus at 23C
      • CS3100: Adhesion Tests at 23C
      • CS3100: Thermal Degradation
    • CS3100 Polysulfide with Phenolic Microballoons
      • CS3100/PMB: Shear Modulus vs Temp
      • CS3100/PMB: Linear CTE vs Temp
      • CS3100/PMB: Young’s Modulus at 23C
      • CS3100/PMB: Bulk Modulus at 23C
      • CS3100/PMB: Adhesion Tests at 23C
    • Arathane 5750 (previously Uralane)
      • 5750: Tensile Modulus vs Temp
      • 5750: Linear CTE vs Temp
    • Arathane 5753 (previously Uralane)
      • 5753: Tensile Modulus vs Temp
      • 5753: Linear CTE vs Temp
      • 5753: Viscosity Increase During Cure
    • EN11
      • EN11: Viscosity Increase During Cure
      • EN11: Tensile Modulus vs Temp
      • EN11: Linear CTE vs Temp
    • Polycarbonate
      • Polycarbonate: Master Curve
      • Polycarbonate: Linear CTE vs Temp
      • Polycarbonate: Compressive Yield
    • Mylar
      • Mylar: % Crystallinity
      • Mylar: Thermal Degradation
      • Mylar: Linear Strain vs Temp
      • Mylar: Tensile Modulus vs Temp
    • Nylon
      • Nylon: Master Curve
      • Nylon: Strain vs Temp
      • Nylon: Tensile Yield at 0C
    • Rexolite
      • Rexolite: Shear Modulus vs Temp
      • Rexolite: Linear CTE vs Temp
      • Rexolite: Compressive Yield at 23C
    • FR408 Composite
      • FR408: Stiffness Matrix at 23C
      • FR408: Linear CTEs vs Temp
    • 4 lb/ft3 PMDI
      • PMDI-4: Shear Modulus vs Temp
      • PMDI-4: Linear CTE vs Temp
      • PMDI-4: Compressive Yield at 23C
    • 6 lb/ft3 PMDI
      • PMDI-6: Shear Modulus vs Temp
      • PMDI-6: Linear CTE vs Temp
      • PMDI-6: Compressive Yield at 23C
    • 20 lb/ft3 PMDI
      • PMDI-20: Shear Modulus vs Temp
      • PMDI-20: Linear CTE vs Temp
      • PMDI-20: Effect of Postcure
      • PMDI-20: Compressive Yield at 23C
    • 10 lb/ft3 PMDI
      • PMDI-10: Shear Modulus vs Temp
      • PMDI-10: Compressive Yield at 23C
    • 6 lb/ft3 TufFoam
      • TufFoam-6: Shear Modulus vs Temp
      • TufFoam-6: Linear CTE vs temp
      • TufFoam-6: Compressive Yield at 23C
    • 10 lb/ft3 TufFoam
      • TufFoam-10: Shear Modulus vs Temp
      • TufFoam-10: Linear CTE vs Temp
      • TufFoam-10: Compressive Yield at 23C
    • 14 lb/ft3 TufFoam
      • TufFoam-14: Shear Modulus vs Temp
      • TufFoam-14: Linear CTE vs Temp
      • TufFoam-14: Compressive Yield at 23C

Thermosets

DEA Cured

  • 828/DEA
  • 828/DEA/GMB
  • 826/CTBN/DEA
  • 828/CTBN/DEA/GMB
  • 828/DEA/Silica

Z Cured

  • 828/Z
  • 828/Z/Alox
  • 828/Z/Mica

Other SNL Formations

  • ANH2
  • 459
  • 459/GMB
  • 459/Alox
  • 828/D230
  • 828/D230/GMB
  • 828/D230/Alox
  • 828/T403
  • 828/2049

Commercial Systems

  • Hysol FP0107
  • Scotchasts
  • Hysol EA93xx
  • Hysol PC18M
  • Hysol KE4238/HD3475

Contact Us

If you would like more information on polymer properties please contact the email below.