3D Characterization of Porosity in AM 316L SS and its Effect on Mechanical Behavior
Abstract not provided.
Publications
3D Characterization of Porosity in AM 316L SS and its Effect on Mechanical Behavior
Abstract not provided.
3D Registration of Structure, Melt Pool History and Design in AM 316L Stainless Steel
Abstract not provided.
Aggregate Presence and Impact of 3D Defect Populations In AM Stainless Steel
Abstract not provided.
Automated high-throughput tensile testing reveals stochastic process parameter sensitivity
Materials Science and Engineering: A
The mechanical properties of additively manufactured metals tend to show high variability, due largely to the stochastic nature of defect formation during the printing process. This study seeks to understand how automated high throughput testing can be utilized to understand the variable nature of additively manufactured metals at different print conditions, and to allow for statistically meaningful analysis. This is demonstrated by analyzing how different processing parameters, including laser power, scan velocity, and scan pattern, influence the tensile behavior of additively manufactured stainless steel 316L utilizing a newly developed automated test methodology. Microstructural characterization through computed tomography and electron backscatter diffraction is used to understand some of the observed trends in mechanical behavior. Specifically, grain size and morphology are shown to depend on processing parameters and influence the observed mechanical behavior. In the current study, laser-powder bed fusion, also known as selective laser melting or direct metal laser sintering, is shown to produce 316L over a wide processing range without substantial detrimental effect on the tensile properties. Ultimate tensile strengths above 600 MPa, which are greater than that for typical wrought annealed 316L with similar grain sizes, and elongations to failure greater than 40% were observed. It is demonstrated that this process has little sensitivity to minor intentional or unintentional variations in laser velocity and power.
Born Qualified Grand Challenge LDRD Final Report
This SAND report fulfills the final report requirement for the Born Qualified Grand Challenge LDRD. Born Qualified was funded from FY16-FY18 with a total budget of ~$13M over the 3 years of funding. Overall 70+ staff, Post Docs, and students supported this project over its lifetime. The driver for Born Qualified was using Additive Manufacturing (AM) to change the qualification paradigm for low volume, high value, high consequence, complex parts that are common in high-risk industries such as ND, defense, energy, aerospace, and medical. AM offers the opportunity to transform design, manufacturing, and qualification with its unique capabilities. AM is a disruptive technology, allowing the capability to simultaneously create part and material while tightly controlling and monitoring the manufacturing process at the voxel level, with the inherent flexibility and agility in printing layer-by-layer. AM enables the possibility of measuring critical material and part parameters during manufacturing, thus changing the way we collect data, assess performance, and accept or qualify parts. It provides an opportunity to shift from the current iterative design-build-test qualification paradigm using traditional manufacturing processes to design-by-predictivity where requirements are addressed concurrently and rapidly. The new qualification paradigm driven by AM provides the opportunity to predict performance probabilistically, to optimally control the manufacturing process, and to implement accelerated cycles of learning. Exploiting these capabilities to realize a new uncertainty quantification-driven qualification that is rapid, flexible, and practical is the focus of this effort.
Calibrated Monte Carlo Models of Microstructure Evolution for Additive Manufacturing
Abstract not provided.
Correlating Defect Populations with Mechanical Performance in AM Tensile Samples of PH 17-4
Abstract not provided.
Correlation of Porosity Defects with In-situ Pyrometry in AM 316L SS
Abstract not provided.
Corroborating Tomographic Defect Metrics with Processing Parameters & Mechanical Response in Metal AM
Abstract not provided.
Critical Defect Signatures and Impacts on Material Performance for Metal Laser Powder Bed Fusion
Abstract not provided.
Data Analysis for the Born Qualified Grand LDRD Project
This report summarizes the data analysis activities that were performed under the Born Qualified Grand Challenge Project from 2016 - 2018. It is meant to document the characterization of additively manufactured parts and processe s for this project as well as demonstrate and identify further analyses and data science that could be done relating material processes to microstructure to properties to performance.
Defect Detection in Metal Additive Manufacturing Through Application of In-Situ Diagnostics
Abstract not provided.
Defect Detection in Metal Additive Manufacturing Through Application of In-Situ Diagnostics
Abstract not provided.
Defect Signatures for Metal Laser Powder Bed Fusion
Abstract not provided.
Defect Signatures for Metal Laser Powder Bed Fusion
Abstract not provided.
Defect Signatures for Metal Laser Powder-Bed Fusion
Abstract not provided.
Detecting Process Defects in Laser-Powder Bed Fusion
Abstract not provided.
Extreme-Value Statistics Reveal Rare Failure-Critical Defects in Additive Manufacturing
Advanced Engineering Materials
Additive manufacturing enables the rapid, cost effective production of customized structural components. To fully capitalize on the agility of additive manufacturing, it is necessary to develop complementary high-throughput materials evaluation techniques. In this study, over 1000 nominally identical tensile tests are used to explore the effect of process variability on the mechanical property distributions of a precipitation hardened stainless steel produced by a laser powder bed fusion process, also known as direct metal laser sintering or selective laser melting. With this large dataset, rare defects are revealed that affect only ≈2% of the population, stemming from a single build lot of material. The rare defects cause a substantial loss in ductility and are associated with an interconnected network of porosity. The adoption of streamlined test methods will be paramount to diagnosing and mitigating such dangerous anomalies in future structural components.
High Throughput Stochastic Tensile Performance of Additively Manufactured Stainless Steels
Abstract not provided.
High Value Pyrometry-To-Defect Correspondence in Laser Powder Bed Fusion of 316L Stainless Steel
Abstract not provided.
High-throughput stochastic tensile performance of additively manufactured stainless steel
Journal of Materials Processing Technology
An adage within the Additive Manufacturing (AM) community is that “complexity is free”. Complicated geometric features that normally drive manufacturing cost and limit design options are not typically problematic in AM. While geometric complexity is usually viewed from the perspective of part design, this advantage of AM also opens up new options in rapid, efficient material property evaluation and qualification. In the current work, an array of 100 miniature tensile bars are produced and tested for a comparable cost and in comparable time to a few conventional tensile bars. With this technique, it is possible to evaluate the stochastic nature of mechanical behavior. The current study focuses on stochastic yield strength, ultimate strength, and ductility as measured by strain at failure (elongation). However, this method can be used to capture the statistical nature of many mechanical properties including the full stress-strain constitutive response, elastic modulus, work hardening, and fracture toughness. Moreover, the technique could extend to strain-rate and temperature dependent behavior. As a proof of concept, the technique is demonstrated on a precipitation hardened stainless steel alloy, commonly known as 17-4PH, produced by two commercial AM vendors using a laser powder bed fusion process, also commonly known as selective laser melting. Using two different commercial powder bed platforms, the vendors produced material that exhibited slightly lower strength and markedly lower ductility compared to wrought sheet. Moreover, the properties were much less repeatable in the AM materials as analyzed in the context of a Weibull distribution, and the properties did not consistently meet minimum allowable requirements for the alloy as established by AMS. The diminished, stochastic properties were examined in the context of major contributing factors such as surface roughness and internal lack-of-fusion porosity. This high-throughput capability is expected to be useful for follow-on extensive parametric studies of factors that affect the statistical reliability of AM components.
Identification of Defect Signatures in an Additively Manufactured Precipitation-Hardened Stainless Steel
Abstract not provided.
Linking in-situ pyrometry to pores
Abstract not provided.
Linking pyrometry to porosity in additively manufactured metals
Additive Manufacturing
Porosity in additively manufactured metals can reduce material strength and is generally undesirable. Although studies have shown relationships between process parameters and porosity, monitoring strategies for defect detection and pore formation are still needed. In this paper, instantaneous anomalous conditions are detected in-situ via pyrometry during laser powder bed fusion additive manufacturing and correlated with voids observed using post-build micro-computed tomography. Large two-color pyrometry data sets were used to estimate instantaneous temperatures, melt pool orientations and aspect ratios. Machine learning algorithms were then applied to processed pyrometry data to detect outlier images and conditions. It is shown that melt pool outliers are good predictors of voids observed post-build. With this approach, real time process monitoring can be incorporated into systems to detect defect and void formation. Alternatively, using the methodology presented here, pyrometry data can be post processed for porosity assessment.