Equilibrium modulus measured by ARES rheometer using torsion rectangular geometry.
saw cut 3-pt bend apparent fracture toughnesses at various extents of reaction
Reference:
Weeks, T. S.; Adolf, D. B.; McCoy, J. D. Macromolecules 1999; 32: 1918-1922.
| G∞(MPa) | KIC (MPa-m1/2) |
|---|---|
| 8.00 | 3.07 |
| 8.00 | 3.09 |
| 8.00 | 3.11 |
| 8.00 | 3.13 |
| 8.00 | 3.29 |
| 5.70 | 3.59 |
| 5.70 | 3.54 |
| 5.70 | 3.73 |
| 5.70 | 3.86 |
| 5.70 | 3.70 |
| 5.70 | 3.47 |
| 5.10 | 3.68 |
| 5.10 | 3.95 |
| 5.10 | 3.82 |
| 5.10 | 3.88 |
| 5.10 | 3.62 |
| 4.20 | 4.27 |
| 4.20 | 3.99 |
| 4.20 | 4.08 |
| 4.20 | 4.14 |
| 4.20 | 4.01 |
| 2.80 | 4.15 |
| 2.80 | 4.18 |
| 2.80 | 3.84 |
| 2.80 | 3.94 |
| 2.80 | 3.83 |
| 2.30 | 3.68 |
| 2.30 | 3.53 |
| 2.30 | 3.73 |
| 2.30 | 3.46 |
| 2.30 | 3.82 |
| 0.66 | 1.17 |
| 0.66 | 1.19 |
| 0.66 | 1.22 |
| 0.66 | 1.04 |
| 0.66 | 1.06 |
| 0.90 | 1.66 |
| 0.90 | 1.44 |
| 0.90 | 1.34 |
| 0.90 | 1.32 |
| 0.90 | 1.30 |
| 1.70 | 2.75 |
| 1.70 | 2.50 |
| 1.70 | 2.52 |
| 1.70 | 2.66 |
| 1.70 | 2.11 |
| 0.41 | 0.56 |
| 0.41 | 0.47 |
| 0.41 | 0.62 |
| 0.41 | 0.60 |
| 0.41 | 0.83 |
| 0.29 | 0.55 |
| 0.29 | 0.47 |
| 0.29 | 0.62 |
| 0.29 | 0.60 |
| 0.29 | 0.84 |
| 0.16 | 0.31 |
| 0.16 | 0.27 |
| 0.16 | 0.24 |
| 0.16 | 0.33 |
| 0.09 | 0.22 |
| 0.09 | 0.26 |
| 0.09 | 0.26 |